The invention relates to a ground heating board. Comprises the following raw materials in weight portion: 10 straw fiber 30, 30 rice husk fiber 50, 10 sawdust 30, 2 nanometer magnesium hydroxide nano aluminum hydroxide 5 copies, 5 copies, 2 nano Magnesium Oxide 1 3 copies, 3 copies of the 1 nano alumina. The nanometer magnesium hydroxide is a modified nanometer magnesium hydroxide. The application of straw fiber, rice husk fiber and sawdust can keep good warmth retention property. In this application, nanometer aluminium hydroxide is used as auxiliary flame retardant, and the flame retardant coefficient of the ground heating board can be raised, and the fire prevention grade can be reached. In this application, nanometer Magnesium Oxide and nanometer alumina are used as heat conducting fillers, and the heat conduction effect is good.
【技术实现步骤摘要】
一种地暖板
本专利技术涉及一种地暖板。
技术介绍
随着节能环保政策措施的实施,使传统的供热方式面临淘汰的危险。而地暖板因其具有施工方便、干净卫生、便于布置等优点，市场日益扩张。但其亦存在缺点，一是导热效果不理想，浪费能源；二是现有地暖板的材质会存在发生火灾的隐患。因此，有必要提出有效的技术方案，解决上述问题。
技术实现思路
本专利技术针对上述现有技术的不足，提供一种导热效果好、阻燃性能优的地暖板。本专利技术解决上述技术问题的技术方案如下：一种地暖板，包括以下重量份的原料：秸秆纤维10-30份、稻壳纤维30-50份、木屑10-30份、纳米级氢氧化镁2-5份、纳米级氢氧化铝2-5份、纳米级氧化镁1-3份、纳米级氧化铝1-3份。优选地，所述纳米级氢氧化镁为改性的纳米级氢氧化镁。优选地，所述改性的纳米级氢氧化镁的制备方法包括如下步骤：将纳米级氢氧化镁置于乙醇溶液中超声分散15min；再加入戊二酸二甲酯，继续超声分散10min；再静置2-5h；然后微波反应器中反应30-50min，经冷却、过滤、洗涤，得到改性的纳米级氢氧化镁。优选地，所述微波反应器的功率为500-700W。优选地，所述纳米级氢氧化镁和戊二酸二甲酯的质量比为1:0.01-1:0.005。有益效果：本申请中的稻壳纤维为天然高分子化合物，起着骨架作用。本申请中通过秸秆纤维、稻壳纤维和木屑的共同作用，保暖性能良好。本申请中改性的纳米级氢氧化镁的使用，对本申请中提高阻燃性能且使得无机材料纳米级氢氧化镁能够在稻壳纤维中得到很好的分散并与之相容是重要的，纳米级氢氧化铝作为辅助阻燃剂，提升本申请地暖板的阻燃系数，可达到...
【技术保护点】
一种地暖板，其特征在于，包括以下重量份的原料：秸秆纤维10‑30份、稻壳纤维30‑50份、木屑10‑30份、纳米级氢氧化镁2‑5份、纳米级氢氧化铝2‑5份、纳米级氧化镁1‑3份、纳米级氧化铝1‑3份。
【技术特征摘要】
1.一种地暖板，其特征在于，包括以下重量份的原料：秸秆纤维10-30份、稻壳纤维30-50份、木屑10-30份、纳米级氢氧化镁2-5份、纳米级氢氧化铝2-5份、纳米级氧化镁1-3份、纳米级氧化铝1-3份。2.如权利要求1所述的地暖板，其特征在于，所述纳米级氢氧化镁为改性的纳米级氢氧化镁。3.如权利要求2所述的地暖板，其特征在于，所述改性的纳米级氢氧化镁的制备方法包括如下步骤：将纳米...