The present invention relates to a compact set of low smoke halogen-free flame retardant cable sheath material preparation method for a cable, which is characterized in that the matrix resin, flame retardant, silane coupling agent, lubricant and antioxidant in proportion in a high-speed mixer mixing, mixer mixing in the temperature range of 115-130 DEG C, cone double feed feeding machine, double screw extruder, single screw shaping, grinding inHot cutting feed, cyclone separator, vibration sieve and packaging, is a 4G network cable sleeve with low smoke halogen-free flame retardant cable sheath material products; the invention improves the cable sheath material hardness, increase the temperature resistance properties of materials. Technical problems in the cable thermal cycling test -40 ~+80 DEG C in cable sheath often loose solved.
【技术实现步骤摘要】
一种光缆用紧套低烟无卤阻燃电缆护套料的制备方法
本专利技术涉及一种新型电缆护套材料，具体是一种光缆用紧套低烟无卤阻燃电缆护套料的制备方法。
技术介绍
普通光缆护套料的制备一般都是以聚乙烯为基料改性的或以氢氧化铝（镁）为阻燃剂用聚烯烃材料改性的，然而这些类型护套料在室外冷热交替（昼夜温差大）的环境下，由于聚乙烯、聚烯烃材料的收缩性影响，时间长后，造成光缆内芯与护套层松懈，最终因为气隙而渗漏，影响光通讯效果，严重时会减少光缆寿命，造成巨大损失。
技术实现思路
本专利技术的目的就是提供一种在室外冷热交替（昼夜温差大）的环境下，能抵御聚乙烯、聚烯烃材料的收缩性影响，光缆内芯与护套层附着完好，无渗漏，光通讯效果好，光缆寿命长的一种4G网络光缆用紧套低烟无卤阻燃电缆护套料的制备方法。本专利技术的一种光缆用紧套低烟无卤阻燃电缆护套料的制备方法，其特征在于：将基体树脂、阻燃剂、硅烷偶联剂、润滑剂和抗氧剂按配比在高速混合机中均匀混合，在115-130℃的温度区间下经密炼机密炼，锥双喂料机喂料，双螺杆挤出，单螺杆成型，磨面热切造粒，旋风分离机送料，振动筛筛分然后包装，即成4G网络光缆用紧套低烟无卤阻燃电缆护套料成品。本专利技术选用Hytrel料TPEE82D代替普通阻燃护套料的POE树脂，并与EVA和界面相容剂混合制成基体树脂，再与阻燃剂、硅烷偶联剂、润滑剂和抗氧剂按配比在高速混合机中均匀混合，经密炼，挤出，成型，造粒，筛分制备成4G网络光缆用紧套低烟无卤阻燃电缆护套料成品，材料的硬度、耐温性能及光缆护套内层与光缆芯的附着力大为提高，经过试测，原有传统材料在110℃×168h的空...
【技术保护点】
一种光缆用紧套低烟无卤阻燃电缆护套料的制备方法，其特征在于：将基体树脂、阻燃剂、硅烷偶联剂、润滑剂和抗氧剂按配比在高速混合机中均匀混合，在115‑130℃的温度区间下经密炼机密炼，锥双喂料机喂料，双螺杆挤出，单螺杆成型，磨面热切造粒，旋风分离机送料，振动筛筛分然后包装，即成4G网络光缆用紧套低烟无卤阻燃电缆护套料成品。
【技术特征摘要】
1.一种光缆用紧套低烟无卤阻燃电缆护套料的制备方法，其特征在于：将基体树脂、阻燃剂、硅烷偶联剂、润滑剂和抗氧剂按配比在高速混合机中均匀混合，在115-130℃的温...