The invention discloses a PVC cable material, which is characterized in that: according to the quality of shares of the polymer material consists of the following components: PVC resin 100 weight portions of the base, need plasticizer: 50-55 weight: 6-8 weight; heat stabilizer; flame retardant agent: 20-30 weight: filling; 10-20 weight. The invention has the advantages that: from the above table, the invention has good mechanical properties and heat resistance of the invention embodies a PVC cable material is good; the oxygen index is greater than 30, indicating the invention is a kind of flame retardant materials; by adding a certain amount of flame retardant and smoke suppressant to capture agent the present invention, burning smoke less, less harmful gas.
【技术实现步骤摘要】
一种pvc电缆料技术背景本专利技术涉及一种pvc电缆料，具体涉及一种耐热阻燃级低烟低卤pvc电缆料。
技术介绍
pvc电缆料是一种以聚氯乙烯树脂为主体，加入必要的助剂为增塑剂、热稳定性、润滑剂及填料等经混合、塑化、切粒而得的一种塑料粒子。其主要用于电线电缆的外层皮履，具有较好的机械性能和电绝缘性能。该类产品一般仅能适用于普通的场合，如果用于高层建筑、化工厂、核电站等特殊环境，将会存在着安全隐患，由于电缆群密集铺设，纵横交错，一旦发生大灾，扑救工作十分困难。因为该类产品一是耐热性相对较低，二是由于pvc树脂通过加入增塑剂后遇火燃烧，即使有些产品加入了一定量的阻燃剂，但遇火燃烧时会放出大量有害、窒息性烟雾。因此对pvc电缆料，消烟有时阻燃要求更为重要。
技术实现思路
本专利技术的目的是为了克服上述缺陷，提供了一种耐热阻燃级低烟低卤的pvc电缆料。为解决上述技术问题，本专利技术的一种pvc电缆料，其创新点在于：按质量份数该高分子材料有以下组分构成：pvc树脂为100重量份；增塑剂：50-55重量份；热稳定剂：6-8重量份；阻燃抑烟剂：20-30重量份；填料：10-20重量份。本专利技术中增塑剂要求具有更高耐热性、低挥发性、分子量较大，此类增塑剂有偏苯三酸三辛酯(TOTM)、均苯四酸四辛酯(TOPM)、双季戊四醇酯、聚酯等。本专利技术选择的增塑剂为偏苯三酸三辛酯和双十三酯；热稳定剂为铅盐热稳定剂；阻燃抑烟剂为Sb2O3、硼酸锌、氢氧化铝、氢氧化镁，Sb2O3为3重量份，硼酸锌为4重量份，氢氧化铝和氢氧化镁为30重量份。本专利技术制备pvc电缆料的工艺，由pvc、偏苯三酸三辛...
【技术保护点】
一种pvc电缆料，其特征在于：按质量份数该高分子材料由以下组分构成：以pvc树脂100重量份为基数，需要增塑剂：50‑55重量份；热稳定剂：6‑8重量份；阻燃抑烟剂：20‑30重量份；填料：10‑20重量份。
【技术特征摘要】
1.一种pvc电缆料，其特征在于：按质量份数该高分子材料由以下组分构成：以pvc树脂100重量份为基数，需要增塑剂：50-55重量份；热稳定剂：6-8重量份；阻燃抑烟剂：20-30重量份；填料：10-20重量份。2.根据权利要求1所述的pvc电缆料，其特征在于：其中的增塑剂为偏苯三酸三辛酯和双十三酯。3.根据权利要求1所述的pvc电缆料，其特征在于：其...
【专利技术属性】
技术研发人员：李春花，
申请(专利权)人：青岛祥智电子技术有限公司，
类型：发明
国别省市：山东,37