The invention discloses an in-situ bionic preparation method and application of composite titanium dioxide nanometer material, relating to the fields of nanometer science, material science, electrochemical sensing, etc.. The invention uses the supramolecular metal gel formed by tannic acid and transition metal ion as the precursor, and in situ prepared the composite titanium dioxide nanometer material on the surface of the glass electrode. The formation of Supramolecular Gel Composite tannic acid good load capacity can achieve a variety of nano materials and titanium dioxide, its modification has a wide application prospect in the field of electrochemical luminescence and optical chemical sensors on the surface of a glass electrode in situ.
【技术实现步骤摘要】
一种复合二氧化钛纳米材料的原位仿生制备方法及应用
本专利技术涉及纳米科学、材料科学、电化学传感等领域，具体涉及一种复合二氧化钛纳米材料的原位仿生制备方法及应用。
技术介绍
近年来，以光作为激发信号，以光电流作为检测信号的光电化学传感器，在生物和环境分析等领域受到了广泛关注。光电化学传感器将传统的电化学传感器和光电化学结合起来，同时具有电化学和光化学传感器的优点。电极表面修饰的光电层在吸收光子后被激发，所产生的载流子发生电荷分离和电子迁移，进而产生光电流。通过采用不同形式的能量作为激发信号和检测信号，使激发和检测信号互不干扰，因而背景信号较低，可获得较高的灵敏度；另一方面，由于采用电化学检测，因而具有设备简单、价廉，易于微型化的优点。光电化学传感器在功能结构上包括光电转换单元和传感识别单元两部分，因此，光电层的材料选择和传感识别策略是目前构建光电化学传感器的两大研究热点。前者主要在于选择具有较好光电化学活性和稳定性的光电活性物种来构建光电转换层，后者主要在于通过不同的分析传感策略来实现对目标物的检测。可用于光电转换层的材料主要包括有机光电分子、导电高分子、无机半导体及其复合材料等。有机光电分子单独作为光电转化层所产生的光电流较弱，需要与其他传导材料进行复合，以提高光电流信号和检测的灵敏度。无机半导体材料是目前研究和应用最为广泛的一类光电材料。该类材料可以通过多种方法制得，并可以通过形貌和尺寸控制表现出优异的光电化学性质。由于量子限域效应的存在，无机纳米半导体材料具有比块体材料更优异的光电化学活性。其中TiO2以其较好的稳定性、较快的电荷传导速率等优点受到了广...
【技术保护点】
一种复合二氧化钛纳米材料的原位仿生制备方法，其特征在于，包括以下步骤：（1）将含有20～50 mg的纳米材料溶液与200～400 µL质量分数为50～200 mg·mL
【技术特征摘要】
1.一种复合二氧化钛纳米材料的原位仿生制备方法，其特征在于，包括以下步骤：（1）将含有20～50mg的纳米材料溶液与200～400µL质量分数为50～200mg·mL-1的单宁酸的二甲基亚砜或水溶液混合，超声震荡5分钟，单宁酸的水溶液需要用浓度为1mol·L-1的氢氧化钠溶液将pH调为7；（2）将上述混合溶液与20～100µL质量分数为40%的二(2-羟基丙酸)二氢氧化二铵合钛的水溶液混合，涡旋震荡1分钟，得到纳米材料掺杂的前躯体溶胶；（3）将20µL步骤（2）制得前躯体溶胶滴在ITO导电玻璃上，...
【专利技术属性】
技术研发人员：马洪敏，魏琴，张勇，吴丹，王欢，庞雪辉，胡丽华，范大伟，杜斌，
申请(专利权)人：济南大学，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。