The invention discloses a spandex spandex fabric, mainly by the composition, which is characterized in that: the menthol, camphor, eucalyptus oil, eugenol, Methylis salicylas made from mixture of microcapsules, and then press 1:0.01 in spandex masterbatch in a volume ratio of 0.1 is added into the microcapsules after mixing, drawing the formation of spandex fiber, spandex fiber weave fabric. The advantages of the cool and refreshing fabric are that the spandex itself has certain cool and slippery features, but in the hot summer, the cool degree is not enough, and the function of refreshing the brain can not be achieved. The invention is used for coating the mixed liquid on the spandex, and is made into the form of slow releasing microcapsule, so that the spandex fabric is more cool and more refreshing in summer.
【技术实现步骤摘要】
一种氨纶面料
本专利技术涉及一种面料，具体是一种由氨纶构成的面料。
技术介绍
随着人们生活水平的提高，在家纺、服装领域，对面料舒适性的追求也越来越高。随着地球的变暖，特别是夏天，对面料的凉爽性也有了一定的要求。为了满足该要求，市场上也有相关的研究，但是，在面料中，针对不同的成分会有不同的要求，目前，市场上还没有关于氨纶的清凉面料的报导。
技术实现思路
本专利技术的主要任务在于提供一种清凉面料，具体是一种无毒、清凉效果自然的清凉面料。为了解决以上技术问题，本专利技术的一种清凉面料，主要由氨纶构成，其特征在于：先将薄荷脑、樟脑、桉油、丁香酚、水杨酸甲酯混合后制成微胶囊，然后在氨纶母粒中按1:0.01-0.1的体积比加入上述微胶囊混合均匀后，拉丝形成氨纶纤维，将上述氨纶纤维织造成面料。进一步地，所述薄荷脑：樟脑：桉油：丁香酚：水杨酸甲酯的质量比为：50:20:10:5:15。本专利技术的优点在于：氨纶本身具有一定的凉、滑特征，但是，在炎热的夏天，凉爽程度不够，且不能起到醒脑的作用。本专利技术在氨纶上镀上述混合液，并制成缓释微胶囊的形式，让氨纶制的面料在夏天更清凉、穿着更神清气爽。具体实施方式先将薄荷脑：樟脑：桉油：丁香酚：水杨酸甲酯按质量比为：50:20:10:5:15进行微胶囊的制作，该制作为常规的方法。在氨纶母粒中按体积比为1:0.01-0.1的体积比加入上述微胶囊混合均匀后，拉丝形成氨纶纤维，将上述氨纶纤维织造成面料。由该工艺制得的清凉面料，其清凉保持周期能达4-9个月。完全能满足一个夏季的使用。
【技术保护点】
一种氨纶面料，主要由氨纶构成，其特征在于：先将薄荷脑、樟脑、桉油、丁香酚、水杨酸甲酯混合后制成微胶囊，然后在氨纶母粒中按1:0.01‑0.1的体积比加入上述微胶囊混合均匀后，拉丝形成氨纶纤维，将上述氨纶纤维织造成面料。
【技术特征摘要】
1.一种氨纶面料，主要由氨纶构成，其特征在于：先将薄荷脑、樟脑、桉油、丁香酚、水杨酸甲酯混合后制成微胶囊，然后在氨纶母粒中按1:0.01-0.1的体积比加入上述微胶囊混合均匀后...
【专利技术属性】
技术研发人员：王宝根，
申请(专利权)人：绍兴柯桥万丰针纺原料有限公司，
类型：发明
国别省市：浙江,33