Polypropylene (PP) is a non-polar crystalline plastic. It is one of the five main types of plastics. It is rich in raw materials, cheap and easy to process and shape. Therefore, it is widely used. Although polypropylene has many advantages, there are also some disadvantages. The biggest drawback is poor cold tolerance. It is easy to break at low temperature, with high shrinkage, poor creep resistance, poor dimensional stability and unstable properties. Make up for PP deficiency by nano modification. Nano superfine talc powder reinforced polypropylene material, the weight ratio of the raw materials of polypropylene: 80 ~ 90; ultrafine talcum powder: 5 ~ 15; silane coupling agent: 0.5 ~ 1.5: 1 ~ 3; antioxidant; light stabilizer: 1 ~ 2; dispersant: 1 ~ 2.
【技术实现步骤摘要】
纳米超细滑石粉增强聚丙烯材料
本专利技术属聚丙烯材料生产
，改善聚丙烯原有的不足。生产出符合社会需求的产品。
技术介绍
聚丙烯(PP)为非极性的结晶塑料，是五大类通用塑料之一，原料来料丰富、价格便宜、易于加工成型等等，因此用途非常广泛。尽管聚丙烯有众多优点，但是，也存在一些不足之处。最大的缺点是耐寒性差。低温易断，且收缩率大，抗蠕变性差，制品尺寸稳定性差，易变性。通过纳米改性来补足PP本身不足之处。
技术实现思路
本专利技术的目的是提供一种不影响材料的力学性能，环保的聚丙烯专用改性料。纳米超细滑石粉增强聚丙烯材料，由下列重量比的原料组成：聚丙烯：80～90；超细滑石粉：5～15；硅烷偶联剂：0.5～1.5；抗氧剂：1.0～3.0；光稳定剂：1.0～2.0；分散剂：1.0～2.0。本专利技术中，所述抗氧剂为乙烯-辛烯的共聚物，所述分散剂为工业白油10#。所述纳米超细滑石粉增强聚丙烯材料的制备方法为：将各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为90-100℃，二区为150-180℃，三区为200-210℃，四区为200-205℃；五区为190-200℃，停留时间为1-2分钟，压力为10-15Mpa。具体实施方式下面通过具体实施方式对专利技术做进一步说明，以下实施例是对本专利技术进行说明而非加以限定。实施例1(1)按重量比分别称取各原料如下：聚丙烯：80；超细滑石粉：5；硅烷偶联剂：0.5；抗氧剂：1.0；光稳定剂：1.0；分散剂：1.0。(2)将各种原料在高速混合器中干混3-5...
【技术保护点】
纳米超细滑石粉增强聚丙烯材料，其特征在于，由下列重量比的原料组成：聚丙烯：80～90；超细滑石粉：5～15；硅烷偶联剂：0.5～1.5；抗氧剂：1.0～3.0；光稳定剂：1.0～2.0；分散剂：1.0～2.0。
【技术特征摘要】
1.纳米超细滑石粉增强聚丙烯材料，其特征在于，由下列重量比的原料组成：聚丙烯：80～90；超细滑石粉：5～15；硅烷偶联剂：0.5～1.5；抗氧剂：1.0～3.0；光稳定剂：1.0～2.0；分散剂：1.0～2.0。2.根据权利要求1所述的纳米超细滑石粉增强聚丙烯材...
【专利技术属性】
技术研发人员：吴佳，
申请(专利权)人：青岛信合一工贸有限公司，
类型：发明
国别省市：山东,37