The invention discloses a high toughness tearing resistance of crumb rubber modified asphalt waterproofing membrane with material, which is composed of the weight of raw materials: 40 asphalt 60, 5 10100 gypsum whisker 200 waste tire rubber powder 10 15, solid content is 30 40% neoprene latex 5 10, 3 linear phenolic resin 5, polysorbate 80 1 1.5, 0.3 0.5 polyethylene wax, the concentration of calcium chloride solution 0.5% 1% 0.5 1 4 8, cashew nut oil. The asphalt material modified by the rubber powder modified waterproof coiled material has the advantages of uniform and high stability, good durability, high toughness, good tear resistance, low cost, long service life, and economical and practical.
【技术实现步骤摘要】
一种高韧性耐撕裂废旧橡胶粉改性防水卷材用沥青材料及其制备方法
本专利技术涉及改性沥青
,尤其涉及一种高韧性耐撕裂废旧橡胶粉改性防水卷材用沥青材料及其制备方法。
技术介绍
沥青作为石油加工的副产物,现阶段已成为公路、机场、建筑等领域中主要铺筑材料和防水材料,随着沥青防水卷材的出现,因其可实现产业化生产,使用方便,在建筑施工中应用越来越受到人们的青睐,特别是楼房顶层天面、地铁天面和堤坝涵闸顶面的施工,将改性沥青卷材带有粘合剂的一面直接粘贴到混凝土表面以达到防水的目的。同时随着我国废旧轮胎的产生量越来越多,大量废旧轮胎的处理问题给我们带来严峻的考验,由于再生胶的环保性问题严重限制了其发展,取而代之的生产胶粉已成为各国利用废旧橡胶的主要手段。目前,胶粉主要应用领域是改性沥青的生产。将废旧轮胎加工成橡胶粉并掺入沥青中用于修建公路以及生产防水材料,既可以提高沥青的使用性能,又能使废旧轮胎变废为宝,解决环保问题,一举多得。由于废胶粉是经过化学或机械加工而制成,其表面是由被破坏的空间网络的网络端组成,其表面呈不规则的毛刺状且布满围观裂纹,因此橡胶粉改性沥青材料的加工过程中,橡胶粉与沥青之间没有形成均匀的体系,结构较为松散,容易发生开裂,影响材料的耐久性。有必要通过预先对胶粉对沥青进行活化后改性处理来提高橡胶粉改性沥青材料的相容性和稳定性。
技术实现思路
本专利技术目的就是为了弥补已有技术的缺陷,提供一种价格低廉,均一、稳定性高,耐久性好,使用寿命长的高韧性耐撕裂废旧橡胶粉改性防水卷材用沥青材料及其制备方法。本专利技术是通过以下技术方案实现的:一种高韧性耐撕裂废旧橡胶粉改 ...
【技术保护点】
一种高韧性耐撕裂废旧橡胶粉改性防水卷材用沥青材料,其特征在于,其是由下述重量份的原料制得:沥青40‑60,石膏晶须5‑10,100‑200目废旧轮胎橡胶粉10‑15,固含量为30‑40%的氯丁胶乳5‑10,线性酚醛树脂3‑5,聚山梨酯‑80 1‑1.5,聚乙烯蜡0.3‑0.5,质量浓度为0.5%‑1%的氯化钙水溶液0.5‑1,腰果壳油4‑8。
【技术特征摘要】
1.一种高韧性耐撕裂废旧橡胶粉改性防水卷材用沥青材料,其特征在于,其是由下述重量份的原料制得:沥青40-60,石膏晶须5-10,100-200目废旧轮胎橡胶粉10-15,固含量为30-40%的氯丁胶乳5-10,线性酚醛树脂3-5,聚山梨酯-801-1.5,聚乙烯蜡0.3-0.5,质量浓度为0.5%-1%的氯化钙水溶液0.5-1,腰果壳油4-8。2.根据权利要求1所述的一种高韧性耐撕裂废旧橡胶粉改性防水卷材用沥青材料的制备方法,其特征在于,包括以下步骤:(1)将废旧轮胎橡胶粉依靠电磁加热结合螺旋输送的塑化装置实现初步断硫并冷却后得...
【专利技术属性】
技术研发人员:唐帆,丁春年,王平,张继云,黄健,
申请(专利权)人:安徽世界村新材料有限公司,
类型:发明
国别省市:安徽,34