Preparation method of polyvinyl alcohol coating of the invention discloses a method for photographic paper, which comprises the following steps: (1) according to the weight ratio of 10 11:1 prepared water and polyvinyl alcohol as raw material; (2) adding water mixer, turn on the blender to stir; (3) adding polyvinyl alcohol, stirring for 5 minutes, to make it fully dispersed in water instead of agglomerating; (4) steam heating to 85 95 DEG C, and to maintain the temperature, stirring until completely dissolved 60min raw materials; (5) to stop steam heating, let the solution of natural cooling to 40 DEG C, i.e.. The invention provides a preparation method of polyvinyl alcohol paint used for photographic paper. The method has simple steps and good dispersibility of polyvinyl alcohol paint.
【技术实现步骤摘要】
一种应用于相纸的聚乙烯醇涂料的配制方法
本专利技术涉及纸业加工领域，具体为一种应用于相纸的聚乙烯醇涂料的配制方法。
技术介绍
适用于广告、影像制作包括喷墨打印所使用的相纸原纸结构包括由纯木浆制备成的、具有白度高、平滑度高和表观细腻度高且无尘埃点的基材和设置于其一面或两面的PE膜和吸墨成像层构成。其中所述的吸墨成像层由纳米级三氧化二铝粉末层构成或通过水溶性的聚乙烯醇(PVA)材料构成，由于聚乙烯醇是一种无毒并且容易分解的材料，因此被广泛应用。
技术实现思路
为解决
技术介绍
提到的问题，本专利技术提出如下技术方案：一种应用于相纸的聚乙烯醇涂料的配制方法，包括如下步骤：(1)按照重量比为10-11:1准备水和聚乙烯醇原料；(2)将水加入搅拌器中，打开搅拌器开始搅拌；(3)加入聚乙烯醇，搅拌5分钟，使其充分分散于水中而不是结块成团；(4)蒸汽加热至85-95℃，并维持此温度，继续搅拌60min，直至原料完全溶解；(5)停止蒸汽加热，让溶液自然冷却至40℃，即得。进一步的，步骤(5)的冷却过程中，每间隔4h搅拌一次，每次2min。本专利技术提出的一种应用于相纸的聚乙烯醇涂料的配制方法，步骤简单，制得的聚乙烯醇涂料分散性好。具体实施方式：为了使本领域的技术人员更好地理解本专利技术的技术方案，下面对本专利技术作进一步说明：一种应用于相纸的聚乙烯醇涂料的配制方法，一种应用于相纸的聚乙烯醇涂料的配制方法，包括如下步骤：(1)按照重量比为10-11:1准备水和聚乙烯醇原料；(2)将水加入搅拌器中，打开搅拌器开始搅拌；(3)加入聚乙烯醇，搅拌5分钟，使其充分分散于水中而不是结块成团；...
【技术保护点】
一种打印纸加工中的聚乙烯醇原料的配制方法，包括如下步骤：(1)按照重量比为10‑11:1准备水和聚乙烯醇原料；(2)将水加入搅拌器中，打开搅拌器开始搅拌；(3)加入聚乙烯醇，搅拌5分钟，使其充分分散于水中而不是结块成团；(4)蒸汽加热至85‑95℃，并维持此温度，继续搅拌60min，直至原料完全溶解；(5)停止蒸汽加热，让溶液自然冷却至40℃，即得。
【技术特征摘要】
1.一种打印纸加工中的聚乙烯醇原料的配制方法，包括如下步骤：(1)按照重量比为10-11:1准备水和聚乙烯醇原料；(2)将水加入搅拌器中，打开搅拌器开始搅拌；(3)加入聚乙烯醇，搅拌5分钟，使其充分分散于水中而不是结块成团；(4)蒸汽加热至85-...
【专利技术属性】
技术研发人员：顾劲松，
申请(专利权)人：安徽文峰特种纸业有限公司，
类型：发明
国别省市：安徽,34