The invention relates to the field of passivation technology, in particular to a stainless steel pickling passivation agent, in accordance with the mass fraction meter comprises the following components: Twelve sodium 5-10, acetic anhydride 10-15, two sodium hydrogen phosphate 5-12, sodium zinc phosphate 20-30, magnesium 10-20, epoxy stearic acid ester 4-10, sodium nitrate 15-25, 8-15 phenyl acid sodium, calcium chloride 4-9. Using the above formula, pickling and passivation agent of the invention of stainless steel, has excellent removal rate, and it can form a layer of dense oxide film on the surface of stainless steel, stainless steel can be protected for a long time, to prevent the surface oxide production again.
【技术实现步骤摘要】
一种不锈钢酸洗钝化剂
本专利技术涉及钝化剂
，特别是一种不锈钢酸洗钝化剂。
技术介绍
钝化液能使金属表面呈钝态的溶液。一般用于镀锌、镀镉和其他镀层的镀后处理。目的是在镀层表面形成能阻止金属正常反应的表面状态，提高其抗蚀性，并增加产品美观。通过配方分析可知常用的钝化液主要成分是铬酸、硝酸、硫酸。但由于铬酸造成环境污染，在某些场合，产品要求银白色或蓝白色，则经三酸钝化处理后生成的彩虹色钝化膜，还可以再经过碱液漂白处理(白色钝化)，但镀层的耐蚀性能下降。
技术实现思路
本专利技术需要解决的技术问题是提供一种不锈钢酸洗钝化剂。为解决上述的技术问题，本专利技术的一种不锈钢酸洗钝化剂，按照质量份数计包括以下组分：十二烷基苯磺酸钠5-10份，乙酸酐10-15份，磷酸氢二钠5-12份，磷酸锌钠20-30份，硝酸镁10-20份，环氧硬脂酸辛酯4-10份，硝酸钠15-25份，苯基酸钠8-15份，氯化钙4-9份。进一步的，按照质量份数计包括以下组分：十二烷基苯磺酸钠5份，乙酸酐10份，磷酸氢二钠5份，磷酸锌钠20份，硝酸镁10份，环氧硬脂酸辛酯4份，硝酸钠15份，苯基酸钠8份，氯化钙4份。进一步的，按照质量份数计包括以下组分：十二烷基苯磺酸钠10份，乙酸酐15份，磷酸氢二钠12份，磷酸锌钠30份，硝酸镁20份，环氧硬脂酸辛酯10份，硝酸钠25份，苯基酸钠15份，氯化钙9份。进一步的，按照质量份数计包括以下组分：十二烷基苯磺酸钠8份，乙酸酐11份，磷酸氢二钠8份，磷酸锌钠22份，硝酸镁12份，环氧硬脂酸辛酯5份，硝酸钠18份，苯基酸钠10份，氯化钙5份。进一步的，按照质量份数计...
【技术保护点】
一种不锈钢酸洗钝化剂，其特征在于，按照质量份数计包括以下组分：十二烷基苯磺酸钠5‑10份，乙酸酐10‑15份，磷酸氢二钠5‑12份，磷酸锌钠20‑30份，硝酸镁10‑20份，环氧硬脂酸辛酯4‑10份，硝酸钠15‑25份，苯基酸钠8‑15份，氯化钙4‑9份。
【技术特征摘要】
1.一种不锈钢酸洗钝化剂，其特征在于，按照质量份数计包括以下组分：十二烷基苯磺酸钠5-10份，乙酸酐10-15份，磷酸氢二钠5-12份，磷酸锌钠20-30份，硝酸镁10-20份，环氧硬脂酸辛酯4-10份，硝酸钠15-25份，苯基酸钠8-15份，氯化钙4-9份。2.按照权利要求1所述的一种不锈钢酸洗钝化剂，其特征在于，按照质量份数计包括以下组分：十二烷基苯磺酸钠5份，乙酸酐10份，磷酸氢二钠5份，磷酸锌钠20份，硝酸镁10份，环氧硬脂酸辛酯4份，硝酸钠15份，苯基酸钠8份，氯化钙4份。3.按照权利要求1所述的一种不锈钢酸洗钝化剂，其特征在于，按照质量份数计包括以下组分：十二烷基苯磺酸钠1...