The invention relates to a gypsum, belonging to the technical field of building materials. A plaster, which is characterized in that: made of the following raw materials in weight portion: gypsum powder, superfine sand 12-18 3-6 parts, 2-3 parts of borax and 2-3 portions of cement, glass fiber 4-7, stearic acid, polyvinyl alcohol latex emulsion 1-2 0.5-1 parts, 0.2-0.8 parts, paraffin emulsion waterproof agent 3-5, peach 2-6. The invention of gypsum, gypsum powder easily combined with super fine sand, enhances the strength of gypsum, and performance into stearic acid emulsion and wax emulsion can change the hydrophilic properties of gypsum, gypsum changed into hydrophobic properties, adding waterproofing agent, improve the water resistance of gypsum, gypsum for the good water resistance and strength high assurance applications of gypsum.
【技术实现步骤摘要】
一种石膏
本专利技术涉及一种石膏，属于建筑材料
技术介绍
石膏属于气硬性胶凝材料，适合做轻质墙体材料，具有生产能耗低，工艺性能好等优点，但石膏也存在弱点：耐水性差，强度较差，建筑体一般要求材料的耐水性好，强度较高，石膏的耐水性差、强度较差限制了石膏在建筑领域的应用。
技术实现思路
本专利技术的目的在于解决已有石膏不能满足需求的不足，提供一种耐水性好、强度高的石膏。本专利技术的一种石膏是通过以下技术方案实现的：一种石膏，采用如下重量份的原料制成：石膏粉12-18份、超细砂3-6份、硼砂2-3份、水泥2-3份、玻璃纤维4-7份、硬脂酸乳液1-2份、聚乙烯醇乳液0.5-1份、石蜡乳液0.2-0.8份、防水剂3-5份、桃胶2-6份；优选的，石膏粉14份、超细砂5份、硼砂3份、水泥2份、玻璃纤维5份、硬脂酸乳液1份、聚乙烯醇乳液1份、石蜡乳液0.6份、防水剂4份、桃胶4份。本专利技术的石膏，石膏粉容易与超细砂结合，增强了石膏的强度，同时入硬脂酸乳液和石蜡乳液能够改变石膏的性能，将石膏的亲水性质改变成憎水性质，防水剂的加入，提高了石膏的耐水性，因此石膏耐水性好、强度高，保证了石膏的应用范围。具体实施方式以下通过实施例形式，对本专利技术的上述内容再作进一步的详细说明，但不应将此理解为本专利技术上述主题的范围仅限于以下的实例，凡基于本专利技术上述内容所实现的技术均属于本专利技术的范围。实施例1：一种石膏，采用如下重量份的原料制成：石膏粉12份、超细砂3份、硼砂2份、水泥2份、玻璃纤维4份、硬脂酸乳液1份、聚乙烯醇乳液0.5份、石蜡乳液0.2份、防水剂3份、桃胶2份。...
【技术保护点】
一种石膏，其特征在于： 采用如下重量份的原料制成：石膏粉12‑18份、超细砂3‑6份、硼砂2‑3份、水泥2‑3份、玻璃纤维4‑7份、硬脂酸乳液1‑2 份、聚乙烯醇乳液0.5‑1份、石蜡乳液0.2‑0.8份、防水剂3‑5份、桃胶2‑6份。
【技术特征摘要】
1.一种石膏，其特征在于：采用如下重量份的原料制成：石膏粉12-18份、超细砂3-6份、硼砂2-3份、水泥2-3份、玻璃纤维4-7份、硬脂酸乳液1-2份、聚乙烯醇乳液0.5-1份、石蜡乳液0.2-0.8份、防水剂3-5份、桃胶...