The present invention discloses a new wear-resistant electric power fittings with flame retardant nylon composite material, made from the following raw materials in weight portion: nylon 6679 83, 15, 13 terpene resin carbon fiber 27, 25 melamine cyanurate 8.5 8.7, 21 24 silicon nitride, light calcium carbonate, UV 9 7 0.3, 0.1 photoabsorbers phenyltriethoxysilane 8 9, 4, 3 propylene glycol aramid pulp 9 10, potato powder 4 5, the invention uses melamine cyanurate as flame retardant, the silicon nitride silane modified as conductive filler, carbon fiber as reinforcing material with other effective components of each composite prepared electric tensile strength, hardness and wear resistance are better.
【技术实现步骤摘要】
本专利技术涉及复合材料
，尤其涉及一种新型耐磨电力金具用阻燃尼龙复合材料及其制作方法。
技术介绍
电力金具是连接和组合电力系统中的各类装置，起到传递机械负荷、电气负荷及某种防护作用的金属附件，作为输电线路上不可或缺的部件，其电能损耗一直是电力部门关注的问题。除了从电力金具铸造工艺上改进外，对其材料的选择尤为重要，目前制备材料主要以无磁性铝合金为主，虽然与以前使用的铁磁性材料相比，对电网节能减排起到一定作用，但是作为金属导体，涡流损耗依然存在，电能损失仍然无法避免，而且铝合金制品必须经过选矿、开采、电解、熔炼等高能耗、高污染工序获得，属于国家限制发展行业，不能满足输电线路的经济需求。用绝缘材料代替金属材料，就可减少涡流损耗，达到更好的节能效果。随着新兴材料科学的迅猛发展，具有绝缘性的复合材料越来越多地被应用到电力行业中，将其作为电力金具的制作材质，将达到减少甚至消除涡流损耗的目的。众所周知纤维增强复合材料具有轻质、高强、耐蚀、绝缘、环保等性能，在电力行业输配电网络中已有广泛应用，因而为了解决输配电线路中钢和铝合金金具高能耗的问题，降低线路损耗，文献《改性复合材料间隔棒和悬垂线夹的研制及应用》对数十种工程塑料进行了遴选和研究，确定以PA66尼龙作为复合材料的基材。在基材中加入玻璃纤维、增韧剂、耐臭氧和耐腐蚀等改性材料，并通过反复试验测试和配方优化，成功研制出一种改性复合材料，并进行了基于改性复合材料的间隔棒和悬垂线夹设计、试制与试验研究，结果表明其性能满足国家标准和电力行业标准要求，基于复合材料的悬垂线夹已应用于35kV和220kV架空输电线路中，运行...
【技术保护点】
一种新型耐磨电力金具用阻燃尼龙复合材料，其特征在于，由下列重量份的原料制成：尼龙66 79‑83、萜烯树脂13‑15、碳纤维25‑27、三聚氰胺氰尿酸盐8.5‑8.7、氮化硅21‑24、轻质碳酸钙7‑9、紫外光吸收剂0.1‑0.3、苯基三乙氧基硅烷8‑9、丙二醇3‑4、芳纶浆粕9‑10、马铃薯全粉4‑5。
【技术特征摘要】
1.一种新型耐磨电力金具用阻燃尼龙复合材料，其特征在于，由下列重量份的原料制成：尼龙6679-83、萜烯树脂13-15、碳纤维25-27、三聚氰胺氰尿酸盐8.5-8.7、氮化硅21-24、轻质碳酸钙7-9、紫外光吸收剂0.1-0.3、苯基三乙氧基硅烷8-9、丙二醇3-4、芳纶浆粕9-10、马铃薯全粉4-5。2.根据权利要求1所述的一种新型耐磨电力金具用阻燃尼龙复合材料的制作方法，其特征在于包括以下步骤：（1）将马铃薯全粉加入10-12倍质量的水中搅拌混匀加热煮沸，保持温度加入轻质碳酸钙、丙二醇继续搅拌10-20分钟，冷却至45-55℃，加入三聚氰胺氰尿酸盐超声分散20...
【专利技术属性】
技术研发人员：余炜，于水，马世虎，
申请(专利权)人：马鞍山市华能电力线路器材有限责任公司，
类型：发明
国别省市：安徽;34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。