The invention relates to a cable fire prevention technology, in particular to a powdery material used for fire prevention of cable holes. Although the existing fire blocking mud has good sealing performance, it has many problems, such as high cost, short time of fire resistance, cracking, short shelf life and so on. The invention provides a fireproof cable hole with powdered material, which consists of the following raw materials by weight percentage: 75% to 85% magnesia powder, dry clay powder 6% ~ 10%, SiO2 2%, powder 1% ~ six sodium hexametaphosphate 5% ~ 6%, lime powder 4% ~ 2% and 2% ~ 3% refractory fiber. The powdery material of the invention has the advantages of long shelf life, low cost and low cost.
【技术实现步骤摘要】
本专利技术涉及电缆防火技术，具体涉及一种电缆孔防火封堵用粉状料。
技术介绍
目前电缆孔一般使用预先制作好的封堵膏泥做防火封堵，封堵膏泥的制作工艺较为复杂，通常使用有机合成树脂作为粘合剂、添加防火剂、耐火油性材料、复合填料等，经辗压捣打而成。可塑性很好，可以任意地进行孔洞以及孔隙封堵。这种堵料主要应用在建筑管道和电线电缆贯穿孔洞的防火封堵工程中，并与无机防火堵料、阻火包配合使用。此类防火封堵泥虽然有良好的封堵性能但是存在以下缺陷：（1）制作原料较为昂贵，制作成本高。（2）耐火时间短，耐火时间只有3小时左右。（3）干燥后会产生裂纹。（4）膏泥保质期较短，长时间放置后会发生硬化现象，导致无法使用。
技术实现思路
本专利技术的目的在于提供一种电缆孔防火封堵用粉状料，相对于现有的防火膏泥，成本得到降低、耐火时间长、保质期长，同时封堵后不产生裂纹。专利技术的配方方案如下，一种电缆孔防火封堵用粉状料，由以下原料按重量百分比组成：镁砂粉75%～85％、干粘土粉6%～10％、SiO2微粉1%～2％、六偏磷酸钠5%～6％、生石灰粉2%～4％、耐火纤维2%～3％。优选的，镁砂粉的粒度不低于200目、干粘土粉的粒度不低于380目。优选的，耐火纤维的纤维长度为4mm～6mm。优选的，一种电缆孔防火封堵用粉状料，由以下原料按重量百分比组成：镁砂粉78%～80％、干粘土粉8%～9％、SiO2微粉1.5%～1.8％、六偏磷酸钠5.4%～6.2％、生石灰粉2.3%～4％、耐火纤维2%～3％。进一步优选的，一种电缆孔防火封堵用粉状料，由以下原料按重量百分比组成：镁砂粉79.5％、干粘土粉8.7...
【技术保护点】
一种电缆孔防火封堵用粉状料，其特征在于，由以下原料按重量百分比组成：镁砂粉75% ～ 85％、干粘土粉6% ～ 10％、SiO2微粉1% ～ 2％、六偏磷酸钠5% ～ 6％、生石灰粉2% ～ 4％、耐火纤维2% ～ 3％。
【技术特征摘要】
1.一种电缆孔防火封堵用粉状料，其特征在于，由以下原料按重量百分比组成：镁砂粉75%～85％、干粘土粉6%～10％、SiO2微粉1%～2％、六偏磷酸钠5%～6％、生石灰粉2%～4％、耐火纤维2%～3％。2.根据权利要求1所述的一种电缆孔防火封堵用粉状料，其特征在于：所述的镁砂粉的粒度不低于200目、干粘土粉的粒度不低于380目。3.根据权利要求1所述的一种电缆孔防火封堵用粉状料，其特征在于：所述的耐火纤维的纤维长度为4mm～6mm。4...
【专利技术属性】
技术研发人员：桂永林，
申请(专利权)人：安徽新盾消防设备有限公司，
类型：发明
国别省市：安徽;34