The present invention relates to electrical equipment parts making material technical field, in particular to a U PVC/ABS modified alloy material comprises the following raw materials produced by weight ratio: PVC:90 ~ 110; hard calcium zinc stabilizer: 3 ~ 3.8; processing aids: 0 ~ 3; compatibilizer: 8 ~ 11; heat ABS:22 ~ 30; composite lubricant: 0.8 ~ 1.8. The advantages are: through the improvement of feed formula of modified alloy material, the manufacturing of the modified alloy material processed into pipe and other products, VEKA reached a high strength, good toughness, good impact resistance, can use repeatedly the advantages of recycling is also very convenient, effective cost savings, making good products the rate of increase, reduce manufacturing cost, reduce the waste of resources, at the same time, good processability and low cost.
【技术实现步骤摘要】
本专利技术涉及电器设备配件的制作材料的
，尤其是涉及一种用于电器设备配件的U-PVC/ABS改性合金料。
技术介绍
目前传统的改性合金料制造成成品的使用中，存在着很多的缺陷，成品的管件在运输的过程中，为了减少运输成本，方便运输，会将管件进行挤压、折弯等动作，但是使用传统的改性合金料的管件，在上述动作之后，部分管件就会出现形状难以完全复原，管件上出现折痕、压痕，甚至会出现破损的现象，造成管件直接报废，使得制造成本较高，产品的浪费率高居不下。
技术实现思路
针对上述现有技术存在的不足，本专利技术的目的是提供一种维卡高、韧性好，抗冲击、反复利用、可回收方便、加工流动性好，成本低廉的用于电器设备配件的U-PVC/ABS改性合金料。为实现上述的目的，本专利技术提供了以下技术方案：一种U-PVC/ABS改性合金料，包括有如下重量比的原料制作而成：PVC：90～110；硬质钙锌稳定剂：3～3.8；加工助剂：0～3；相容剂：8～11；耐热ABS：22～30；复合润滑剂：0.8～1.8。本专利技术进一步设置为：包括有如下重量比的原料制作而成：PVC：98～100；硬质钙锌稳定剂：3.2～3.5；加工助剂：1.8～3；相容剂：9～10；耐热ABS：24～26；复合润滑剂：1～1.2。通过采用上述技术方案，本专利技术所达到的技术效果为：通过改进改性合金料的原料配方，使得制造后的改性合金料加工成管件等产品上时，达到了维卡高、韧性好，抗冲击强度好、可反复利用的优势，而且回收利用也极其方便，有效节约了成本，使得产品的良品率提升，降低了制造成本，减少了资源的浪费，同时加工流动性好，...
【技术保护点】
一种U‑PVC/ABS改性合金料，其特征在于：包括有如下重量比的原料制作而成：PVC：90～110；硬质钙锌稳定剂：3～3.8；加工助剂：0～3；相容剂：8～11；耐热ABS：22～30；复合润滑剂：0.8～1.8。
【技术特征摘要】
1.一种U-PVC/ABS改性合金料，其特征在于：包括有如下重量比的原料制作而成：PVC：90～110；硬质钙锌稳定剂：3～3.8；加工助剂：0～3；相容剂：8～11；耐热ABS：22～30；复合润滑剂：0.8～1.8。2.根据权...