The invention discloses an automobile water pump magnetic powder metallurgy inner and outer ring and a preparation method thereof, comprises the following components: the mass percentage of raw materials of copper Cu 3 5%, Mn 15%, Ni 10 0.8 1%, Mo 0.8%, MoS2 0.5 0.5 0.6%, silicone resin adhesive 2 3%, more than the amount of base material for stainless steel powder. The invention adopts high density molding, precise temperature control of sintering technology, equipped with automatic powder and die wall lubrication feeding mechanism design and development of advanced mold structure, high precision machining, obtain the acid and alkali resistance, corrosion resistance, high precision stainless steel outer magnetic powder metallurgy parts, good prospects for industrialization.
【技术实现步骤摘要】
本专利技术涉及汽车磁力泵制备领域，具体属于汽车磁力水泵粉末冶金内、外磁环及其制备方法。
技术介绍
随着国际国内汽车产业的不断发展，环境友好、节能减排、绿色新能源汽车的普及率逐年递增，用于新能源车辆的电机、控制器等电器的磁力水泵也将与日俱增，该项目研究开发的不锈钢磁力水泵关键零件内、外磁环，其作为磁力水泵的主要零件，市场规模将日益增大。经市场调查发现，目前在我国国内生产加工技术尚未成熟，磁力水泵不锈钢内、外磁环产品尚未实现量产、大规模销售，多数仍采用德国进口。
技术实现思路
本专利技术的目的是提供一种汽车磁力水泵粉末冶金内、外磁环及其制备方法，采用高密度成型、精确控温烧结技术，开发先进模具结构、设计自动送粉和模壁润滑机构及高精度加工关键装备，获得耐酸、耐碱、耐腐蚀、高精度不锈钢外磁环粉末冶金件，工业化前景良好。本专利技术的技术方案如下：一种汽车磁力水泵粉末冶金内、外磁环，由以下质量百分数原料组分组成：铜Cu3-5%、Mn10-15%、Ni0.8-1%、Mo0.5-0.8%、MoS20.5-0.6%、有机硅树脂粘合剂2-3%，余量为基料不锈钢粉末。一种汽车磁力水泵粉末冶金内、外磁环制备方法，具体的工艺步骤如下：先将上述原料在混料机中充分混合，再采用高密度成型、精确控温烧结技术，同时利用氢气作为保护气氛，使产品充分脱碳，提高材料韧性，最后采用珩磨往复式磨削加工方式，保证内、外磁环光洁度及尺寸精度。本专利技术的有益技术效果如下：1、采用不锈钢粉末为原料，添加铜、锰、镍等金属元素及有机硅树脂粘合剂，在混料机中充分混合，产品成分可控，易切削加工。2、采用高密度成型、精确...
【技术保护点】
一种汽车磁力水泵粉末冶金内、外磁环，其特征在于，由以下质量百分数原料组分组成：铜Cu 3‑5%、Mn 10‑15%、Ni 0.8‑1%、Mo 0.5‑0.8%、MoS2 0.5‑0.6%、有机硅树脂粘合剂 2‑3%，余量为基料不锈钢粉末。
【技术特征摘要】
1.一种汽车磁力水泵粉末冶金内、外磁环，其特征在于，由以下质量百分数原料组分组成：铜Cu3-5%、Mn10-15%、Ni0.8-1%、Mo0.5-0.8%、MoS20.5-0.6%、有机硅树脂粘合剂2-3%，余量为基料不锈钢粉末。2.一种汽车磁力水...
【专利技术属性】
技术研发人员：顾进文，疏金平，张克庆，王元杰，
申请(专利权)人：安徽恒均粉末冶金科技股份有限公司，
类型：发明
国别省市：安徽;34