The present invention relates to one kind of raw material and process for producing No. 70 asphalt from Venezuela Persian crude oil. It includes: crude oil and Bachar Clou crude oil. No. 70 heavy traffic asphalt of the invention accords with the establishment of the \Ministry of transportation production specification for construction of highway asphalt pavement\ in JTGF40-2004 No. 70 a grade road asphalt index, better than the national standard (GB50092-96) index. The CDU straight-run production of high grade road asphalt, the production process is simple, is the most economical and convenient method of asphalt production, product performance and produce excellent, and can completely replace the imported high grade road asphalt, to meet the rapid development of China's road construction and national economic development needs.
【技术实现步骤摘要】
本专利技术属于道路沥青
，具体涉及一种委内瑞拉波斯坎原油生产70号沥青的原料及工艺方法。
技术介绍
近几年来，我国经济的繁荣促进了公路交通事业的高速发展，大批高速公路相继建成或正在兴建，但是我国沥青特别是高等级道路沥青的产量还远远跟不上公路建设的需要，进口沥青仍占有重要的市场份额。由于受国内原油性质的制约，大部分国内原油生产的道路沥青在质量上不能满足要求。一般而言，蜡含量低于2.2％，薄膜烘箱试验15℃延度大于15cm的70号沥青，交通部门才用它作为高等级路面铺装材料。我国原油80％以上属石蜡基原油，含蜡量较高，不宜生产道路沥青。随着我国公路运输交通量急剧增加，超载、重载现象严重，路面结构的损坏情况日益加剧，沥青混凝土高温稳定性不足形成车辙，是我国高等级公路沥青路面的主要病害形式之一。随着进口原油特别是重质原油比例的增加，采用进口重质原油生产重交通道路沥青，具有重要的现实意义。委内瑞拉波斯坎原油属高硫环烷基油，原油密度大，粘度大、凝点低，汽油柴油馏分收率为30％左右，碳氢比及残炭值均较高，其性质类似于一般原油的减压渣油馏分。因该原油酸值、重金属含量高，残炭高，不宜作催化裂化原料，而饱和烃含量低，胶质、沥青质含量高，蜡含量小，很适宜作优质沥青原料。
技术实现思路
本专利技术克服了现有技术中的缺点，提供了一种委内瑞拉波斯坎原油生产70号沥青的原料及工艺方法，该70号重...
【技术保护点】
一种委内瑞拉波斯坎原油生产70号沥青的原料，其特征在于，包括：委内瑞拉波斯坎原油和巴查克罗原油。
【技术特征摘要】
1.一种委内瑞拉波斯坎原油生产70号沥青的原料，其特征在于，包括：委
内瑞拉波斯坎原油和巴查克罗原油。
2.根据权利要求1所述一种委内瑞拉波斯坎原油生产70号沥青的原料，其
特征在于，还包括拉古娜原油。
3.根据权利要求2所述一种委内瑞拉波斯坎原油生产70号沥青的原料，其
特征在于，按重量百分比包括：委内瑞拉波斯坎原油70-90％、巴查克罗
原油5-20％和拉古娜原油2-10％。
4.根据权利要求3所述一种委内瑞拉波斯坎原油生产70号沥青的工艺方
法，其特征在于，包括以下步骤：
a)初顶油汽经初馏塔顶馏出，初馏塔底部的初底油经泵加压进入常压炉加
热后进入常压塔分馏；
b)常顶油经常压塔顶馏出，常压侧线油品经常压塔侧线馏出，常底油经泵
加压进入减压炉加热后进入减压塔分馏；
c)减顶油经减压塔顶抽真空馏出，减压侧线产...
【专利技术属性】
技术研发人员：刘仪凤，蒲旭斌，巫兴朋，黄爱春，官见龙，
申请(专利权)人：佛山高富中石油燃料沥青有限责任公司，
类型：发明
国别省市：广东;44