The present invention provides a cement compound synergist. It is composed of sodium bisulfate 65 - 85%, molasses 10 - 25% and ethylene glycol 5 - 10%. The product of the invention is added into the cement raw material according to the proportion of 0.05% of the weight of the cement raw material, and then grinding, the grinding effect can be improved, the energy consumption of the grinding is reduced, and the grinding efficiency is improved. That is, under the condition of the same fineness of cement, the yield can be increased. Under the same condition of cement output and power consumption of the mill, the specific surface area of cement can be increased, so as to improve the quality of cement. The addition of the product to the cement does not adversely affect the performance of the cement, but can improve the early strength of the cement.
【技术实现步骤摘要】
(一)、所属领域本专利技术涉及的是一种水泥添加剂，具体地说是一种用于水泥生产过程中的水泥添加剂。(二)、
技术介绍
目前说使用的水泥添加剂，大多是水泥出厂之后使用过程中添入，以改善水泥的性能。水泥生产过程中的粉磨工序不仅需要消耗大量的能源，而且粉磨效果不好会直接影响水泥的质量。(三)、
技术实现思路
本专利技术的目的在于提供一种可以降低水泥生产能耗、提高水泥质量的水泥复合增效剂。本专利技术的目的是这样实现的它由重量比为硫酸氢钠65-85％、糖蜜10-25％和乙二醇5-10％组成。将本专利技术的产品按照占水泥原料重量的0.05％的比例加入到水泥原料中再进行粉磨，可以改善粉磨效果，降低粉磨能耗，提高粉磨效率。即在水泥细度相同的条件下，可以增加产量；在水泥产量和磨机功率消耗相同的条件下，能增加水泥的比表面积，从而提高水泥的质量。本专利技术的产品添加到水泥中，不但不会对水泥的性能带来不利影响，相反可以提高水泥的早期强度，实验证明3天抗压强度可提高5-20％，28天抗压强度可提高10％以上，而且耐久性、抗冻性、抗渗性、蒸养效果及干缩性能均优于国内市场销售的水泥外加剂。(四)、具体实施方案下面举例对本专利技术做更详细的描述按重量比为硫酸氢钠(NaHSO4)65-85％、糖蜜10-25％和乙二醇(CH2OH-CH2OH)5-10％的比例将各原料混合制成产品。按重量比为硫酸氢钠(NaHSO4)70％、糖蜜20％和乙二醇(CH2OH-CH2OH)10％的比例将各原料混合制成产品。按重量比为硫酸氢钠(NaHSO4)80％、糖蜜15％和乙二醇(CH2OH-CH2OH)5％的比例将各原料混...
【技术保护点】
一种水泥复合增效剂，其特征是：它由重量比为硫酸氢钠６５－８５％、糖蜜１０－２５％和乙二醇５－１０％组成。
【技术特征摘要】
【专利技术属性】
技术研发人员：孟小柯，孟德华，
申请(专利权)人：阿城市柯强水泥磨剂有限公司，
类型：发明
国别省市：93[中国|哈尔滨]