The invention discloses a preparation method of composite ceramic water reducing agent. (1) sixteen alkyl pyridine water reducing agent of raw materials for organic anionic surfactant twelve sodium dodecyl sulfate or cationic surfactant bromide, with water glass or sodium carbonate as the raw material of inorganic superplasticizer; (2) the raw materials are in accordance with the organic water reducing agent, inorganic water reducing agent is 1 ~ 3, 1 ~ 3 the ratio of the configuration and prepared by ball milling mixing, composite ceramic water reducing agent. The composite ceramic is suitable for building ceramic slurry water reducing agent has the advantages of alleviating effect, Jiening range, energy efficiency and convenient use, is ideal for building ceramic slurry dilution grinding materials.
【技术实现步骤摘要】
本专利技术涉及，特别是一种适合建筑陶瓷坯料泥浆的复合陶瓷减水剂的制备方法。
技术介绍
减少建筑陶瓷坯料泥浆的含水量并提高泥浆的喷雾干燥造粒效率，从而达到降低生产成本，节约能耗的目的是目前建筑陶瓷工业一直需要解决的问题。喷雾干燥工艺要求采用流动性好又无触变性的泥浆，为此，目前建筑陶瓷厂常用的符合原料特性的合适泥浆减水剂有腐质酸钠、鞣型减水剂、亚硫酸纸浆废液、聚丙烯酸钠等。但目前我国建筑陶瓷行业普遍使用的减水剂其减水效果不够理想，泥浆的含水量大部分在33～35％之间，且存在着减水剂加入范围窄，触变性大的缺点。
技术实现思路
本专利技术的目的在于提供一种适合建筑陶瓷坯料泥浆的复合陶瓷减水剂的制备方法。本专利技术以表面活性剂与无机减水剂进行复合配置，按照不同的比例配成有机/无机复合减水剂，制备出了适合建筑陶瓷工业生产需要的复合陶瓷减水剂。具体制备过程包括以下步骤(1)选用阴离子表面活性剂十二烷基磺酸钠或阳离子表面活性剂溴化十六烷基吡啶为有机减水剂原料，选用水玻璃或碳酸钠为无机减水剂原料；(2)将上述原料分别按照有机减水剂无机减水剂为1～3∶1～3的配比进行配置并通过球磨混合均匀，制得复合陶瓷减水剂。本专利技术所制备的适合建筑陶瓷坯料泥浆的复合陶瓷减水剂，具有解凝效果好、解凝范围宽、节能增效和使用方便等优点，是理想的建筑陶瓷泥浆稀释助磨材料。具体实施例方式实施例一 (1)选用50g十二烷基磺酸钠和150g水玻璃为原料；(2)将上述配置好的原料通过球磨混合均匀制成有机/无机复合陶瓷减水剂。实施例二(1)选用50g溴化十六烷基吡啶和50g碳酸钠为原料；(2)将上述配置...
【技术保护点】
一种复合陶瓷减水剂的制备方法，其特征在于其步骤为：（１）选用阴离子表面活性剂十二烷基磺酸钠或阳离子表面活性剂溴化十六烷基吡啶为有机减水剂原料，选用水玻璃或碳酸钠为无机减水剂原料；（２）将上述原料分别按照有机减水剂∶无机减水剂 为１～３∶１～３的配比进行配置并通过球磨混合均匀，制得复合陶瓷减水剂。
【技术特征摘要】
【专利技术属性】
技术研发人员：王海，李惠敏，
申请(专利权)人：桂林工学院，
类型：发明
国别省市：45[中国|广西]