The invention relates to a method for forming a fixed pattern on a ceramic product by cracking glaze and non reactive glaze. It is used to draw the pattern is then dipped in latex, white matt glaze, then tear latex, just in place with white matt coated latex glaze filling, spray crackle glaze. White glaze where there is a small pattern produced, is the place where the effect of the crack filling. The utility model can also be adsorbed on the upright cup and other device types, and is not easy to flow, and overcomes the weakness that the cracked glaze is easy to flow on the cup.
【技术实现步骤摘要】
本专利技术涉及一种。
技术介绍
在裂纹釉与别的釉的搭配应用中,往往难以形成具体的图案,因为裂纹釉有流动的特点。而这项专利技术则克服了裂纹釉这个缺点,而且即使是在杯子等有侧立面的物体上也不会流动。
技术实现思路
本专利技术的目的在于克服上述不足之处,提供一种陶瓷制品上裂纹釉与其他釉和谐共存形成图案的方法。本专利技术的技术方案一种,其特征在于所述方法是A、采用乳胶在陶瓷制品干泥坯上画出图案,将画有图案的陶瓷制品在白色无光反应釉中浸一下提出,无光反应釉附在干坯上的厚度为0.3~0.4mm,B、然后撕掉乳胶,在撕掉乳胶的地方用米白无光反应釉填涂,填涂的釉层厚度为0.3mm~0.4mm;C、最后整体喷少量裂纹釉,(其裂纹釉的浓度为65波美度,喷为点状,每点为0.07~0.11cm2,密度为528点/cm2)送至窑内烧成,其烧制温度为1180~1200℃,烧制时间为3~4个小时,产生了使白色无光釉的地方有小花纹,填涂的地方是裂纹的效果。本专利技术的关键是把无光反应釉转化为裂纹釉,从而改变了单纯由裂纹釉形成图案不够固定的缺点。把白色无光反应釉用别的釉代替也可。但只有米白无光反应釉才有遇裂纹釉产生裂纹这个特性。本专利技术则克服了裂纹釉这个缺点,而且即使是在杯子等有侧立面的物体上也不会流动。具体实施例方式一种,它是采用乳胶在陶瓷制品干泥坯上画出图案,将画有图案的陶瓷制品在白色无光反应釉中浸一下提出,无光反应釉附在干坯上的厚度为0.3mm,然后撕掉乳胶,在撕掉乳胶的地方用米白无光反应釉填涂,填涂的釉层厚度0.4mm。最后整体喷少量裂纹釉,其裂纹釉的浓度为65波美度,喷为点状, ...
【技术保护点】
一种在陶瓷制品上裂纹釉与无光反应釉共存形成图案的方法,其特征在于:A、采用乳胶在陶瓷制品干泥坯上画出图案,将画有图案的陶瓷制品在白色无光反应釉中浸一下提出,无光反应釉附在干坯上的厚度为0.3mm~0.4mm;B、然后撕掉乳胶 ,在撕掉乳胶的地方用米白无光反应釉填涂,填涂的釉层厚度为0.3mm~0.4mmC、最后整体喷少量裂纹釉,其裂纹釉的浓度为65波美度,喷为点状,每点面积为0.07~0.11/cm↑[2],密度为5~8点/cm↑[2],送至窑内烧成,其 烧制温度为1180~1200℃,烧制时间为3~4个小时,产生了白色无光釉的地方有小花纹,填涂的地方是裂纹的效果。
【技术特征摘要】
【专利技术属性】
技术研发人员:潘俊明,徐娅,
申请(专利权)人:湖南泰鑫瓷业有限公司,
类型:发明
国别省市:43[中国|湖南]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。