The invention discloses a preparation method of foaming concrete lightweight wall material, concrete is coagulation components according to weight ratio of water to cement, sand (or fly ash or coal cinder can) ratio equal to 0.8 to 1 to 1, respectively, water, ordinary cement and sand are arranged in the mixing tank mixing; composition of foaming agent in the weight ratio of rosin: sodium hydroxide: bovine glue is equal to 15: 1: 18 ratio, respectively, rosin, sodium hydroxide and bovine glue is arranged inside the container and mixed evenly, prepared by the foaming agent; foaming agent and water for 1 to 50 of the proportion, respectively. Foaming agent and foaming water into the tank, with an air pump to foam tank pressure to 8kg, the foaming agent under high pressure foaming gun into the concrete mixing tank mixing, the foaming stability The formation of foam concrete, foam concrete will be injected into the mold, the natural curing to stripping stripping strength requirements, after 8 hours (25 C) maintenance is formed after the density of 700 - 900kg / M = 3 foaming concrete lightweight wall material.
【技术实现步骤摘要】
【技术保护点】
一种发泡混凝土轻质墙体材料的制备方法,其特征在于混凝土按组成成份重量比为水∶普通水泥∶中砂(或粉煤灰,或工业煤渣均可)等于0.8∶1∶1的比例,分别将水、普通水泥和中砂置于搅拌罐中充分搅拌均匀;发泡剂的组成成分按重量比为松香∶氢氧化钠∶牛胶等于15∶1∶18的比例,分别将松香、氢氧化钠和牛胶置于容器内混合搅拌均匀,制得发泡剂;按发泡剂与水为1∶50的比例,分别将发泡剂和水注入发泡罐内,用普通气泵向发泡罐加压至8kg,把高压下的发泡剂用发泡枪注入混凝土搅拌罐中充分搅拌均匀,使其发泡稳定后形成发泡混凝土。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。