The invention discloses a method for preparing magnesium niobate ferroelectric materials, which is characterized with lead oxide (PbO), Magnesium Oxide (MgO) and five (two Nb: niobium oxide 2 O: 5) as raw materials, according to the molar ratio of 3: 1: 1 of the dose ratio after mixing, grinding machine grinding screw into the 3 to 6 hours; or the raw materials in the same proportion, the mixture is added with deionized water immersion will the mixture amount, evenly mixed grinding in a mortar, in the oven, at 80 to 100 DEG C baking to slightly dry, and then put into the screw grinding the grinding machine in 3 ~ 8 hours, can get the lead magnesium niobate ferroelectric materials, the general formula: Pb (Mg: 1 / 3 / 2 / 3 Nb: O): 3. The invention has the advantages of simple process, easy operation, short preparation time, simple phase, good dispersivity and uniform particles.
【技术实现步骤摘要】
本专利技术涉及铁电材料的制备，特别是。技术背景自从铁电材料发现以来，随之而来的材料制备和应用技术上的拓展和提 高促进了其在工业和商业领域的广泛应用。在众多已发掘的铁电材料中，含铅的化合物，如PZT (锆钛酸铅)、P薩(铌镁酸铅)、PLZT (锆钛酸铅镧)等， 由于具有优异的介电和电至伸縮特性，在高技术应用领域中扮演着极为重要 的角色。目前，在铅系铁电材料的制备工艺中，高温煅烧及研磨是必不可少 的，而高温煅烧过程极易导致氧化铅的挥发，从而使所制得的材料的化学组 成发生改变和烧绿石杂相的出现；而研磨方式均基于粉碎理论设计，在合成 新型的无机非金属材料上显得力不从心，合成一个无机非金属固体材料往往 需要球磨几十个小时，而且得到的是无定形相，还需要附加退火工艺来获得 所希望的物相。由于传统制备方法的局限性和不完善，导致了铅系铁电材料 合成工艺效率低，能耗高，产率低。
技术实现思路
本专利技术的目的是针对现有技术的不足而提供的一种铌镁酸铅铁电材料的 制备方法，该方法无需高温煅烧而且改变了传统的研磨方式，具有简单，高 效，能耗低等特点。实现本专利技术目的的具体技术方案是，它是以氧化铅(Pb0)、氧化镁(Mg0) 和五氧化二铌(Nb205)为原料，按其摩尔比为3:1:1的剂量比混合后，放 入螺杆研磨机中研磨3 6小时；或者将上述原料按同样比例混合后，在混合物中加入将其混合物浸没量的去离子水，在研钵中研磨混合均匀后，放入烘箱中，在80 10(TC下烘至微干，然后放入螺杆研磨机中研磨3 8小时，即可得到铌镁酸铅铁电材料，其一般式为Pb (Mg1/3Nb2/3) 03 。...
【技术保护点】
一种铌镁酸铅铁电材料的制备方法，其特征在于它是以氧化铅（ＰｂＯ）、氧化镁（ＭｇＯ）和五氧化二铌（Ｎｂ↓［２］Ｏ↓［５］）为原料，按其摩尔比为３∶１∶１的剂量比混合后，放入螺杆研磨机中研磨３～６小时；或者将上述原料按同样比例混合后，在混合物中加入将其混合物浸没量的去离子水，在研钵中研磨混合均匀后，放入烘箱中，在８０～１００℃下烘至微干，然后放入螺杆研磨机中研磨３～８小时，即可得到铌镁酸铅铁电材料，其一般式为：Ｐｂ（Ｍｇ↓［１／３］Ｎｂ↓［２／３］）Ｏ↓［３］。
【技术特征摘要】
【专利技术属性】
技术研发人员：李强，陈诚，孟婧，褚晶，张敏，
申请(专利权)人：华东师范大学，
类型：发明
国别省市：31[中国|上海]