The invention relates to a building material, in particular to a concrete early strength agent prepared from filtrate in the production of a concrete water reducing agent by using pulp waste liquid. The present invention by weight of its basic composition is: the residue of 30 ~ 60%, fly ash 20 ~ 40%, 2 ~ 5%, three ethanol ammonia (anhydrous sodium sulfate or anhydrous sodium sulfate) from 20 to 40%. The present invention utilizes the waste liquid from papermaking waste liquor to produce slag in the process of producing lignin sulfonate concrete water reducing agent, and makes \waste into treasure\ to produce the concrete early strength agent, and eliminates the two pollution.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料，特别是一种利用纸浆废液生产混凝土 减水剂过程中的滤渣制备生产的混凝土早强剂。
技术介绍
造纸厂生产纸浆后排放的废液(亦称黑液或红液)，可制成木质 素磺酸盐混凝土减水剂，已为业内人士所熟知。目前，国内应用造纸 废液生产木质素磺酸盐混凝土减水剂，在生产过程中经过滤产生的滤渣一般都作为废物弃之不用，其数量约占浆液总量的10%左右，造成 二次固体废弃物污染。滤渣的主要成分为NA2SH4，本专利技术应用该废 渣、粉煤灰、三乙醇氨、元明粉(硫酸钠)等材料进行复配加工，生 产混凝土早强剂。
技术实现思路
本专利技术所要解决的技术问题是提供一种"变废为宝"，利用造纸废液生产木质素磺酸盐混凝土减水剂后的滤渣，复配生产混凝土早强 剂。掺加该混凝土早强剂，混凝土具有显著的早强、防冻和增强效果。而且该早强剂完全符合GB8076-1997《混凝土外加剂》国家标准。 本专利技术的混凝土早强剂，按重量计其基本组成为滤渣 30~60%粉煤灰 20~40%三乙醇氨 2~5% 元明粉(硫酸钠或无水硫酸钠) 20~40%本专利技术混凝土早强剂其复配实例如下 配比1滤渣 30%粉煤灰 28%三乙醇氨 2%元明粉 40% 配比2滤渣 45%粉煤灰 22%三乙醇氨 3%元明粉 30% 配比3滤渣 60%粉煤灰 15%三乙醇氨 5%元明粉 20%本专利技术的优点是利用造纸废液生产木质素磺酸盐混凝土减水剂 过程中的滤渣，"变废为宝"生产混凝土早强剂，杜绝二次污染。例如配制1M"昆凝土应用饮用水 150kg水泥 260 kg砂子 715 kg石子 1160 kg粉煤灰 40 kg...
【技术保护点】
一种利用纸浆废液生产混凝土减水剂过程中的滤渣制备生产的混凝土早强剂，其特征是：按重量计其基本组成为 滤渣 ３０～６０％ 粉煤灰 ２０～４０％ 三乙醇氨 ２～５％ 元明粉（硫酸钠或无水硫酸钠） ２０～４０％。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。