本发明专利技术属于无机非金属材料及其制备技术领域，特别涉及一种锂基铸瓷口腔修复材料及其制备方法。该材料的化学组成成分（重量％）为：Ｌｉ↓［２］Ｏ　１７～２４％、Ａｌ↓［２］Ｏ↓［３］　１０～１５％、ＳｉＯ↓［２］　５５～６５％、Ｋ↓［２］Ｏ　４～６％、Ｎａ↓［２］Ｏ　０．５～３％、ＺｒＯ↓［２］０．５～４％以及着色剂氧化物０．５～３％。其中ＳｉＯ↓［２］与Ｌｉ↓［２］Ｏ的摩尔比为１．２～１．８∶１。着色剂氧化物为Ｆｅ↓［２］Ｏ↓［３］、ＭｎＯ↓［２］、ＣｅＯ↓［２］中的任意一种或一种以上。该铸瓷口腔修复材料的制备方法包括如下具体步骤：备料、熔制、水淬、粉碎、喷雾干燥、成型、烧结。本发明专利技术与现有技术相比具有成本低、尺寸精度高、产品重复性好、产品质量稳定、力学综合性能优良，适用于工业化生产的优点。

Lithium based casting porcelain oral restorative material and preparation method thereof

The invention belongs to the field of inorganic non-metallic materials and the preparation technology thereof, in particular to a lithium base casting porcelain oral restorative material and a preparation method thereof. Chemical composition of the material (wt%): Li: 2 O 17 to 24% Al, 2 O:: 3 10 ~ 15% SiO, down 2 from 55 to 65%, down K 2 O 4 ~ 6%, Na: 2 O 0.5 ~ 3% ZrO: 2, 0.5 ~ 4% and 0.5 ~ 3% oxide colorants. The molar ratio of SiO: 2 and Li: 2 O 1.2 - 1.8: 1. Fe: colorant oxide 2 O: 3, MnO: 2, CeO: 2 in any one or more. The preparation method of ceramic dental restorative materials comprising the following steps: preparation, melting, quenching, grinding, spray drying, molding and sintering. Compared with the prior art, the present invention has the advantages of low cost, high dimensional accuracy, good product repeatability, stable product quality, excellent mechanical comprehensive performance and suitability for industrial production.

【技术实现步骤摘要】

【技术保护点】
一种锂基铸瓷口腔修复材料，其特征在于该材料的化学组成成分（重量％）为：Ｌｉ↓［２］Ｏ１７～２４％、Ａｌ↓［２］Ｏ↓［３］１０～１５％、ＳｉＯ↓［２］５５～６５％、Ｋ↓［２］Ｏ４～６％、Ｎａ↓［２］Ｏ０．５～３％、ＺｒＯ↓［２］０．５～４％以及着色剂氧化物０．５～３％。

【技术特征摘要】

【专利技术属性】
技术研发人员：梁新杰，仇越秀，周少雄，宋文娟，冯金海，李晓天，高振英，孙梦依，
申请(专利权)人：安泰科技股份有限公司，北京安泰生物医用材料有限公司，
类型：发明
国别省市：11[中国|北京]