低温模造光学玻璃制造技术

本发明专利技术是一种低温模造光学玻璃，该玻璃由按重量百分比为Ｐ↓［２］Ｏ↓［５］９～２５％、ＧｅＯ↓［２］１～２０％、Ｎｂ↓［２］Ｏ↓［５］１２～２８％、ＴｉＯ↓［２］１～７％、Ｂｉ↓［２］Ｏ↓［３］０～５５％、ＷＯ↓［３］０～３８％、ＳｉＯ↓［２］０～３％、Ｂ↓［２］Ｏ↓［３］０～５％、Ａｌ↓［２］Ｏ↓［３］０～２％、Ｔａ↓［２］Ｏ↓［５］０～３％、Ｓｂ↓［２］Ｏ↓［３］０～１％、总合不超过１３％的Ｒ↓［２］Ｏ（Ｒ是Ｌｉ、Ｎａ、Ｋ），及总合不超过１５％的ＸＯ（Ｘ是Ｃａ、Ｓｒ、Ｂａ、Ｚｎ）的成分组成。本发明专利技术低温模造玻璃不含氧化铅、氧化砷等对环境有害的成分，而且易于生产、在软化点附近温度不会发生失透。

Low temperature molding optical glass

The present invention relates to a low temperature molding optical glass, the glass is composed by weight percent: P 2 O: 5, GeO: 9 ~ 25% 2 1 ~ 20% Nb, 2 O: 5: 12 ~ 28% TiO, down 2 from 1 to 7%. Bi: 2 O: 3, WO: 0 ~ 55% 3 0 ~ 38% SiO, down 2 from 0 to 3%, down B 2 O down 3 from 0 to 5%, down Al 2 O down 3 from 0 to 2%, Ta: 2 O was down 5 from 0 to 3%, down Sb 2 O down 3 from 0 to 1%, total no more than 13% R: 2 O (R, Na, K, Li), and a total of not more than 15% XO (X, Sr, Ba, Ca Zn). Composition. The low temperature molding glass of the invention does not contain harmful components of the environment, such as lead oxide, arsenic oxide, etc., and is easy to be produced, and the temperature can not be lost near the softening point.

【技术实现步骤摘要】

【技术保护点】
一种光学玻璃，其成份按重量百分比计算至少包含有：Ｐ↓［２］Ｏ↓［５］９～２５％、ＧｅＯ↓［２］１～２０％、Ｎｂ↓［２］Ｏ↓［５］１２～２８％、ＴｉＯ↓［２］１～７％、Ｂｉ↓［２］Ｏ↓［３］０～５５％、总合不超过１３％的Ｒ↓［２］Ｏ，其中Ｒ可以是Ｌｉ、Ｎａ及Ｋ，以及总合不超过１５％的ＸＯ，其中Ｘ可以是Ｃａ、Ｓｒ、Ｂａ及Ｚｎ。

【技术特征摘要】

【专利技术属性】
技术研发人员：蔡宗岳，石翔仁，
申请(专利权)人：亚洲光学股份有限公司，
类型：发明
国别省市：71[]