A high strength inorganic glass steel tub and a preparation method thereof, with Magnesium Oxide and magnesium chloride as main raw material, together with other accessories, made into a slurry of perfusion in the bathtub mold, room temperature curing, spraying Fangci paint -- cold porcelain surface grinding, demoulding, finishing, which has the performance of it. The bathtub made by the formula and the preparation method of the invention has the advantages of light weight, low cost, good heat insulation property, high compression resistance, wear resistance, strong impact resistance, acid and alkali resistance, etc.. The utility model is suitable for hotels, restaurants and family health use.
【技术实现步骤摘要】
本专利技术涉及一种。目前，利用已有技术生产制造的浴盆，大多为铸铁、陶瓷、搪瓷、水泥等品种，有的生产工艺较复杂、需烧结，有的重量较大，成本较高，保温性能差，均存在许多不足之处。本专利技术的目的是提供一种以氧化镁、氯化镁为主要原料，配以其它付料，在模具内常温灌注固化成型的。为实现上述目的，本专利技术采用如下技术方案以氧化镁、氯化镁为主要原料，配以其它付料按比例调配而成料浆灌注于模具内，常温下即可固化成型;其成份组成，按重量由下述成份组成氧化镁 16-18氯化镁 9-11石英砂 16-18珍珠岩 1.5-3.5硫酸亚铁 0.5-1.5玻璃布 3-5水 8.5-11减水剂 0.02-0.03玻璃丝 0.1-0.3一种高强无机玻璃钢浴盆的制备方法1、备模在模具内涂抹减水剂;2、铺玻璃布在模具内铺一层玻璃布;3、灌注料浆配料制成料浆进行灌注;4、固化成型灌注一定时间后，浴盆在模具内常温固化成型;5、脱模硬化将成型浴盆脱模，放置自然硬化，再抹平内外表面;6、打磨干燥对内外表面不平处进行整理打磨，使浴盆内表面较光滑，继续进行自然干燥;7、喷涂冷瓷涂料对浴盆内表面进行喷涂冷瓷涂料，喷涂后的浴盆内表面达到瓷面的性能效果。由于采用上述配方及制备方法，使本专利技术的高强无机玻璃钢浴盆具有重量轻、成本低、保温性能好、抗压、耐磨、抗冲击力大、光泽度高、耐酸碱等优点。以下结合实施例对本专利技术作进一步的描述1、备模使用一套钢模、分为上模、下模，均为浴盆形状，在上模的底部有灌注口，先在上、下模内涂抹一层减水剂0.02-0.03kg，以利于脱膜。2、铺玻璃布在下棋的...
【技术保护点】
一种高强无机玻璃钢浴盆，其特征在于，按重量由下述成份组成：氧化镁１６－１８氯化镁９－１１石英砂１６－１８珍珠岩１．５－３．５硫酸亚铁０．５－１．５玻璃布３－５水８．５－１１减水剂０．０２－０．０３玻璃丝０．１－０．３。
【技术特征摘要】
【专利技术属性】
技术研发人员：苏玉祥，苏玉书，苏桂凤，孙秀华，
申请(专利权)人：河北省沧县杜林新型建筑装璜材料厂，
类型：发明
国别省市：13[中国|河北]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。