The invention relates to a dual-purpose glass cutting and grinding process and the method of making glass cutting dual-purpose saw, production method is: 20 to 30 portions of iron powder, copper powder from 40 to 50, 10 to 20 portions of tin, nickel powder with 5 to 10 copies, 60 / 80MBD6 mixed in diamond a play, and placed in the mold, heating in 700 - 800 DEG C, the pressure is 25 35MPa, formed in 250 350MPa under the pressure of the prepared alloy knife head of impregnated diamond particles, the impregnated diamond particles of the alloy knife head firmly with steel matrix in welding that can be made of glass cutting and grinding blade. Due to the use of fine-grained diamond particles, and the metal composition suitable collocation, also has the characteristics of cutting and grinding, capable of efficiently processing glass, and the face smooth without burr, save again grinding process, compared with the traditional glass cutter, processing efficiency is increased by 2 times, the cost decreased by 30%.
【技术实现步骤摘要】
本专利技术涉及一种玻璃切磨锯片,尤其涉及一种对玻璃进行切割及磨边加工的两用锯片;同时,本专利技术还涉及一种该玻璃切磨两用锯片的制作方法。
技术介绍
目前,装饰用玻璃在使用过程中均需要进行切割(修边、倒角)、磨边等工作,现有的加工方法所使用的工具一般分为两种水刀和玻璃刀。水刀为大型机械,无法在终端市场进行修边、倒角工作;玻璃刀小巧,使用起来较为方便,但是只适合于划线,由于是人力操作,工作效率低,采用此种方式无法进行倒角、磨边等工作,且折断后的断面毛糙,必须再次打磨。
技术实现思路
针对上述问题,本专利技术的目的在于提供一种可同时进行切割和磨边工作的两用锯片。同时,本专利技术的目的还在于提供一种该玻璃切磨两用锯片的制作方法。为了达到上述目的,本专利技术的技术方案在于提供了一种玻璃切磨两用锯片,该锯片由基体和孕镶有金刚石颗粒的合金刀头组成,合金刀头由下列重量份数的成分组成铁粉20~30份铜粉40~50份锡粉10~20份镍粉5~10份金刚石 60/80MBD6所述的基体为钢基体。所述的合金刀头为一环形,合金刀头固定焊接在基体的外周边缘上。同时,本专利技术的技术方案还在于提供一种玻璃切磨两用锯片的制作方法,将铁粉20~30份,铜粉40~50份,锡粉10~20份,镍粉5~10份,金刚石60/80MBD6均匀混合在一起,并放入模具内,在700-800℃的温度下加热,热压压力为25-35Mpa,在250-350Mpa的压力下成型,制得孕镶有金刚石颗粒的合金刀头,最后将孕镶有金刚石颗粒的合金刀头与钢基体牢固焊接在一起,即可制得玻璃切磨两用锯片。所述的基体为钢基体。所述的合 ...
【技术保护点】
一种玻璃切磨两用锯片,其特征在于:该锯片由基体和孕镶有金刚石颗粒的合金刀头组成,合金刀头由下列重量份数的成分组成:铁粉20~30份铜粉40~50份锡粉10~20份镍粉5~10份金刚石60/80MBD6。
【技术特征摘要】