The present invention relates to the technical field of lubricating coatings, especially for lubricating coating a steel plate, in accordance with the mass fraction meter comprises the following components: ammonia methyl acid ethyl ester 20-35, silicon paste 5-10, acrylate polymer 5-13, vinyl acetate 10-15, hydrophobic silica 4-10, two stearyl amine 10-15 two. Epichlorohydrin 10-15, Teflon 5.6-8.3, acrylate 1.8-3.3. Using the above formula, lubricating coating of the invention can make the steel plate, galvanized steel sheet has lower friction coefficient, can improve the formability of steel plates, and has good corrosion resistance and coating performance; in addition, the invention of low cost components, convenient for popularization and application.
【技术实现步骤摘要】
本专利技术涉及润滑涂料
，特别是一种钢板用润滑涂料。
技术介绍
润滑涂料，实际上是在要求润滑的部件表面上形成一层润滑剂的覆盖膜(俗称粘结固体干膜润滑剂/BSLF)来代替润滑油膜，以便满足某些不能使用油脂润滑的润滑要求。它的适用范围比较广，从1000℃以上的白热高温到液态氢的深冷温度；从化学工业的腐蚀环境到受强辐射的在月球表面工作的机械都能有效地润滑，已被广泛应用于航天器、飞机、卫星、火箭、原子能设备、仪器仪表、车辆、船舶等领域。
技术实现思路
本专利技术需要解决的技术问题是提供一种钢板用润滑涂料。为解决上述的技术问题，本专利技术的一种钢板用润滑涂料，按照质量份数计包括以下组分：氨甲基酸乙酯20-35份，硅膏5-10份，丙烯酸酯聚合物5-13份，乙酸乙烯酯10-15份，疏水白炭黑4-10份，二硬脂酰二乙胺10-15份，环氧氯丙烷10-15份，聚四氟乙烯5.6-8.3份，丙烯酸酯1.8-3.3份。进一步的，按照质量份数计包括以下组分：氨甲基酸乙酯20份，硅膏5份，丙烯酸酯聚合物5份，乙酸乙烯酯10份，疏水白炭黑4份，二硬脂酰二乙胺10份，环氧氯丙烷10份，聚四氟乙烯5.6份，丙烯酸酯1.8份。进一步的，按照质量份数计包括以下组分：氨甲基酸乙酯35份，硅膏10份，丙烯酸酯聚合物13份，乙酸乙烯酯15份，疏水白炭黑10份，二硬脂酰二乙胺15份，环氧氯丙烷15份，聚四氟乙烯8.3份，丙烯酸酯3.3份。进一步的，按照质量份数计包括以下组分：氨甲基酸乙酯25份，硅膏6份，丙烯酸酯聚合物11份，乙酸乙烯酯11份，疏水白炭黑6份，二硬脂酰二乙胺12份，环...
【技术保护点】
一种钢板用润滑涂料，其特征在于，按照质量份数计包括以下组分：氨甲基酸乙酯20‑35份，硅膏5‑10份，丙烯酸酯聚合物5‑13份，乙酸乙烯酯10‑15份，疏水白炭黑4‑10份，二硬脂酰二乙胺10‑15份，环氧氯丙烷10‑15份，聚四氟乙烯5.6‑8.3份，丙烯酸酯1.8‑3.3份。
【技术特征摘要】
1.一种钢板用润滑涂料，其特征在于，按照质量份数计包括以下组分：氨甲基酸乙酯20-35份，硅膏5-10份，丙烯酸酯聚合物5-13份，乙酸乙烯酯10-15份，疏水白炭黑4-10份，二硬脂酰二乙胺10-15份，环氧氯丙烷10-15份，聚四氟乙烯5.6-8.3份，丙烯酸酯1.8-3.3份。2.按照权利要求1所述的一种钢板用润滑涂料，其特征在于，按照质量份数计包括以下组分：氨甲基酸乙酯20份，硅膏5份，丙烯酸酯聚合物5份，乙酸乙烯酯10份，疏水白炭黑4份，二硬脂酰二乙胺10份，环氧氯丙烷10份，聚四氟乙烯5.6份，丙烯酸酯1.8份。3.按照权利要求1所述的一种钢板用润滑涂料，其特征在于，按照质量份数计包括以下组分：氨甲基酸乙酯35份，硅膏...