The invention discloses a short fiber reinforced plastic soft belt and its production method, a modified polyethylene resin, E- glass fiber and antioxidants prepared according to the ratio of the raw material, melting into mixing machine mixing, into the granulator, the plasticized mixture flows through the die, cooling after cutting into the fiber aggregate; made of plastic extruder screw barrel extruder, plastic resin by extrusion die, the tension, cooling and sizing, can produce short fiber reinforced plastic hose. By adding a certain amount of fiber component, the invention improves the strength of the plastic soft water band to improve the service life, and has the advantages of simple process and low cost.
【技术实现步骤摘要】
本专利技术涉及塑料加工领域，具体是一种短纤维加强的塑料软水带及其生产方法。
技术介绍
目前市场上销售的塑料软水带有三种：第一种：是聚乙烯编织水带，这种水带是以聚乙烯扁丝编织成筒状，聚乙烯筒料采用粘合剂粘合工艺；第二种：是PVC编织水带，这种水带是以涤纶线编织网挂PVC糊料制成的PVC软水带；第三种：是无纤维聚乙烯软水带（通常称为白龙带）乙烯编织水带及PVC编织软水带的缺点是：工艺复杂，生产效率低，成本高。在生产线上需要绕线机将化纤编织成网，再用塑料挤出工艺成型。而且无纤维聚乙烯软水带，因无纤维加强，相对强度低、寿命短。
技术实现思路
本专利技术的目的在于提供一种短纤维加强的塑料软水带及其生产方法，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种短纤维加强的塑料软水带，由以下质量百分比的原料制备而成：改性聚乙烯树脂73.2～77.2％，E-玻璃纤维20.8～24.8％，抗氧剂1.8～2.2％。作为本专利技术进一步的方案：所述E-玻璃纤维的粒径为9～13μm。一种所述的短纤维加强的塑料软水带的生产方法，其特征在于，具体步骤如下：（1）按配比取各原料，改性聚乙烯树脂熔融后，将熔体以14～30g/min的流动速率加入混料机中，再加入E-玻璃纤维和抗氧剂，混合均匀；（2）将混合均匀的物料送入造粒机造粒，造粒机的料筒温度为160～190℃，模口温度为180～200℃，螺杆转速为30～80转/分钟，经塑化的混合料由模口流出...
【技术保护点】
一种短纤维加强的塑料软水带，其特征在于，由以下质量百分比的原料制备而成：改性聚乙烯树脂73.2～77.2％，E‑玻璃纤维20.8～24.8％，抗氧剂1.8～2.2％。
【技术特征摘要】
1.一种短纤维加强的塑料软水带，其特征在于，由以下质量百分比的原料制备而成：改性聚乙烯树脂73.2～77.2％，E-玻璃纤维20.8～24.8％，抗氧剂1.8～2.2％。
2.根据权利要求1所述的短纤维加强的塑料软水带，其特征在于，所述E-玻璃纤维的粒径为9～13μm。
3.一种如权利要求1所述的短纤维加强的塑料软水带的生产方法，其特征在于，具体步骤如下：
（1）按配比取各原料，改性聚乙烯树脂熔融后，将熔体以14～30g/min的流动速率加入混料机中，再加入E-玻璃纤维和抗...