The invention relates to the technical field of automobile spare parts processing, in particular to a preparation method of a pretreatment agent for spraying the inner wall of an automobile water tank. First, adding 25 phr of furfural resin and 15 water into a container, stirring for 5 minutes; then slowly adding 1.5 hydrochloric acid, stir, add after stirring for 5 minutes; then slowly adding 20 phr of polyacrylate emulsion and 10 parts of water, stir, add after stirring for 5 minutes; and then slowly added 0.3 copies of uronic acid, stir, add after stirring for 5 minutes; finally slowly added 1 potassium chloride and 15 water, stirring for 10 minutes. The preparation method of the invention, the method gradually added, can not only improve the solubility between substances, but also avoid the agglomeration of particles may make pretreatment pretreatment agent was significantly improved.
【技术实现步骤摘要】
本专利技术涉及汽车零部件加工
，具体是涉及一种用于汽车水箱内壁喷涂的预处理剂的制备方法。
技术介绍
为了更好的提高汽车水箱的结构性能以及延长其使用寿命，主要在其内壁喷涂纳米薄膜，以提供其结构强度。但是，由于在其内表面仅喷涂薄膜，而未采用防护膜衬底，喷涂加工后的产品在使用一段时间后，表面的薄膜逐渐的褪去，这样将对汽车水箱的结构性能产生较大影响。
技术实现思路
针对现有技术中存在的技术问题，本专利技术的目的在于提供一种用于汽车水箱内壁喷涂的预处理剂的制备方法，为实现上述目的，本专利技术采用了以下技术方案：一种用于汽车水箱内壁喷涂的预处理剂的制备方法，首先向容器中加入25份糠醛树脂和15份水，搅拌5分钟；接着缓慢加入1.5份盐酸，边加边搅拌，添加完毕后搅拌5分钟；接着缓慢加入20份聚丙烯酸酯乳液和10份水，边加边搅拌，添加完毕后搅拌5分钟；然后缓慢加入0.3份糖醛酸，边加边搅拌，添加完毕后搅拌5分钟；最后缓慢加入1份氯化钾和15份水，搅拌10分钟。本专利技术的有益效果表现在：1）、喷涂方法中使用的预处理剂，其配方设计合理、新颖，特别是添加了少量的糖醛酸，可以显著提高预处理剂的处理效率。通过预处理剂的配合使用，使汽车水箱在后续喷涂聚四氟乙烯纳米薄膜时，聚四氟乙烯纳米薄膜的附着力更强，继而提高产品的使用寿命。2）、预处理剂的制备方法，通过逐步添加的方法，不仅能够提高各物质之间的溶解性能，还能避免颗粒团聚的可能，使预处理剂的预处理能力得到显著的提升。3）、汽车水箱的喷涂方法，操作工艺简...
【技术保护点】
一种用于汽车水箱内壁喷涂的预处理剂的制备方法，其特征在于首先向容器中加入25份糠醛树脂和15份水，搅拌5分钟；接着缓慢加入1.5份盐酸，边加边搅拌，添加完毕后搅拌5分钟；接着缓慢加入20份聚丙烯酸酯乳液和10份水，边加边搅拌，添加完毕后搅拌5分钟；然后缓慢加入0.3份糖醛酸，边加边搅拌，添加完毕后搅拌5分钟；最后缓慢加入1份氯化钾和15份水，搅拌10分钟。
【技术特征摘要】
1.一种用于汽车水箱内壁喷涂的预处理剂的制备方法，其特征在于首先向容器中加入25份糠醛树脂和15份水，搅拌5分钟；接着缓慢加入1.5份盐酸，边加边搅拌，添加完毕后搅拌5分钟；接着缓慢加入2...
【专利技术属性】
技术研发人员：钱根来，
申请(专利权)人：芜湖奕辰模具科技有限公司，
类型：发明
国别省市：安徽;34