A preparation method of side chain containing alkynyl polysiloxane, the method under the protection of nitrogen, the propargyl methyl silane, methyl siloxane ring four, six methyl two siloxane reaction polysiloxane containing alkynyl side chain in alkaline catalytic reaction. The side chain of the invention is formed with the functional group of the alkyne group, and the addition reaction of the alkyne group can be used to obtain different side chain modified products. The method has the advantages of simple process and low cost, and is suitable for industrial production, and the polymer has good application prospect in the preparation of elastomers and in the field of optoelectronic materials.
【技术实现步骤摘要】
本专利技术涉及一种侧链含炔基的聚硅氧烷的制备方法，属支链功能化的聚硅氧烷制备
技术介绍
有机聚硅氧烷是有机高分子中最重要、应用最广泛的一类聚合物，其主链是以Si-O键为重复单元的结构形式，侧基连接不同的有机基团。由于Si-O键非常柔顺，而且键能较大，因此聚硅氧烷具有许多独特的性能，如耐高低温、耐化学试剂、耐候、耐老化、阻燃等等。目前已经在建筑、医药、电气、航空航天等领域均已得到广泛应用，是国民经济中重要而必不可少的新型高分子材料。然而在合成侧链含功能性聚硅氧烷时，最普通的方法是以硅氢加成的方式将各种功能性基团接枝上去如侧链为氟烃基的聚硅氧烷，侧链为氨基的聚硅氧烷，侧链为聚醚的聚硅氧烷等等，但是硅氢加成需要昂贵的重金属催化剂，而且在反应过程中往往需要将各种功能型基团的活泼氢进行保护，待反应完成后再去保护，因而造成反应过程繁琐，增加了生产成本。因此，避免使用贵重金属催化剂是具有支链有机硅聚合物发展的一个方向。
技术实现思路
本专利技术的目的是，针对现有合成侧链含功能性聚硅氧烷技术的不足，提供一种侧链含炔基的聚硅氧烷的制备方法。本专利技术的技术方案是，一种侧链含炔基的聚硅氧烷的制备方法，在氮气保护下，将炔丙基甲基硅烷、甲基环四硅氧烷和六甲基二硅氧烷按照质量为1:10~25:2~10混合均匀，加入碱性催化剂，升温至60~80℃，反应2~6小时后，再进行减压脱除低分子物质得到的，其结构式表示如下：
【技术保护点】
一种侧链含炔基的聚硅氧烷的制备方法，其特征在于，所述方法在氮气保护下，将炔丙基甲基硅烷、甲基环四硅氧烷和六甲基二硅氧烷按照质量为1:10~25:2~10混合均匀，加入碱性催化剂，升温至60~80℃，反应2~6小时后，再进行减压脱除低分子物质得到，其结构式表示如下：式中R为苯基、甲基或乙烯基，n，m为整数，不大于20。
【技术特征摘要】
1.一种侧链含炔基的聚硅氧烷的制备方法，其特征在于，所述方法在氮气保护下，将炔
丙基甲基硅烷、甲基环四硅氧烷和六甲基二硅氧烷按照质量为1:10~25:2~10混合均匀，加
入碱性催化剂，升温至60~80℃，反应2~6小时后，再进行减压脱除低分子物质得到，其结构
式表示如下：
式中R为苯基、甲基或乙烯基，n，m为整数，不大于20。
2.根据权利要求1所述一种侧链含炔基的聚硅氧烷的制备方法，其特征在于，所述炔丙
基甲基硅烷为炔丙基甲基二乙氧基硅烷、炔丙基甲基二甲氧基硅烷中的一种。
...
【专利技术属性】
技术研发人员：游胜勇，陈桂琴，戴润英，陈衍华，夏俊，陈桂华，董晓娜，谌开红，李玲，胡银，严伯刚，
申请(专利权)人：江西省科学院应用化学研究所，
类型：发明
国别省市：江西;36