The invention is a suitable material of anti heat floor brick tunnel kiln, the anti thermal material between the laying floor brick tunnel kiln walking tracks, which comprises the following components: borax as 80~100 weight portions, rice wheat stone powder 80~90 weight portions, aluminum powder in 150~350 weight portions of carbon residue 600~700 weight portions, asbestos powder 200~250 weight portions, 80~90 weight portions of perlite powder. The invention has the advantages of anti heat floor material brick tunnel kiln of the invention; has good heat preservation performance and anti heat performance, adhesion, anti pressure increase and reduce the brick firing time.
【技术实现步骤摘要】
本专利技术涉及一种反热材料,尤其是涉及一种适合砖体隧道窑的反热地铺料。
技术介绍
目前,现有的砖体隧道窑行走轨道中间用水泥混凝土铺设而成垒砖区域,而在经常的高温环境下,水泥混凝土的垒砖区域容易开裂、破损。这样影响砖体的垒放以及烧成的品质。
技术实现思路
本专利技术的目的是提供一种适合砖体隧道窑的反热地铺料。本专利技术解决其技术问题所采用的技术方案是:一种适合砖体隧道窑的反热地铺料,该反热地铺料铺设在砖体隧道窑行走轨道之间,其特征是它包括以下各组分:硼砂为80~100重量份,饭麦石石粉为80~90重量份,铝粉粉为150~350重量份,炭渣为600~700重量份,石棉粉200~250重量份,珍珠岩粉80~90重量份。一种适合砖体隧道窑的反热地铺料,该反热地铺料铺设在砖体隧道窑行走轨道之间,其特征是它包括以下各组分:煤粉50~100重量份、铁屑为80~100重量份,饭麦石石粉为80~90重量份,炭渣粉为150~350重量份,黄铁矿粉300~400重量份,返渣为200~300重量份,石棉粉200~250重量份,珍珠岩粉80~90重量份。本专利技术的有益效果:使用本专利技术的砖体隧道窑的反热地铺料;具有良好的保温性能和反热性能,其附着力、抗压力增加并且减少了砖体烧成时间。具体实施方式实施例1,一种适合砖体隧道窑的反热地铺料,该反热地铺料铺设在砖体隧道窑行走轨道之间,其特征是它包括以下各组分:硼砂为80~100重量份,饭麦石石粉为80~90重量份,铝粉粉为150~350重量份,炭渣为600~700重量份,石棉粉200~250重量份,珍珠岩粉80~90重量份。实施例2,一 ...
【技术保护点】
一种适合砖体隧道窑的反热地铺料,该反热地铺料铺设在砖体隧道窑行走轨道之间,其特征是它包括以下各组分:硼砂为80 ~ 100重量份,饭麦石石粉为80 ~ 90重量份,铝粉粉为150 ~ 350重量份,炭渣为600 ~ 700重量份,石棉粉200 ~ 250重量份,珍珠岩粉80 ~ 90重量份。
【技术特征摘要】
1.一种适合砖体隧道窑的反热地铺料,该反热地铺料铺设在砖体隧道窑行走轨道之间,其特征是它包括以下各组分:硼砂为80~100重量份,饭麦石石粉为80~90重量份,铝粉粉为150~350重量份,炭渣为600~700重量份,石棉粉200~250重量份,珍珠岩粉80~90重量份。2.一种适合砖体隧道窑的反...