A preparation method of Co/ZnO composite material, the deionized water 53gZnCl2, 2gCoCl2 6H2O and 43gNaOH were dissolved in 100mL, and then the 3 kinds of solution in magnetic stirring under the condition of fully mixing 20min into a high-pressure reaction kettle, 8 10h reaction in 105 under 115 DEG C, the reaction kettle products with deionized water and ethanol respectively after 3 times washing centrifuge in 8 10h 70, drying 75 DEG C in a vacuum drying box, i.e.. The beneficial effects of the invention are: simple synthesis process, mild reaction conditions, low production cost, good repeatability, transition metal Co exists in the ZnO gap, lattice or surface, can lead to lattice defects, the hole electron recombination to reduce, thus making ZnO the light absorption enhancement, thus to improve its photocatalytic properties.
【技术实现步骤摘要】
本专利技术涉及材料合成方法，具体的是一种Co/ZnO复合材料的制备方法。
技术介绍
近年来，随着人们生活质量的提高对环境的要求也越来越高，但由于全球工业迅速发展，环境污染已日趋严重，其中水污染已成为威胁人类健康的重要问题因此如何有效地治理水污染就成为当今社会迫切需要解决的难题之一。纳米ZnO作为一种新型的ｎ型半导体材料（Ｅｇ＝3.37eV），因其具有较高的光催化活性，且易制备、无污染、价廉易得和独特的电学及光学性能以及特殊的结构等诸多优点而备受人们的青睐，其对废水中有机污染物有较好的光催化降解效果，是一种常用的光催化剂，但由于纯ZnO带隙较宽使得其只有在较短波长385nm的紫外光照条件下才具有较好的光催化活性，因而大大限制了ZnO作为光催化剂的工业应用。目前可通过改性ZnO如掺杂金属或非金属离子以形成染料敏化或固熔体等方法，进而改变带隙并控制其能带结构，达到提高ZnO光催化活性的目的。李侠等采用金属离子掺杂的方法，分别制备了纳米CeZnO及纳米AgZnO，发现稀土离子Ce及过渡金属离子Ag的掺杂，均可显著提高纳米ＺｎＯ对亚甲基蓝的光催化降解效果。Kong等通过掺杂Ta5+进而提高了ZnO对苯的降解能力。余长林等采用水热处理结合焙烧的方法制备了Zr/ZnO，Al/ZnO及Zr－Al/ZnO，发现ZrAl单独掺杂及Zr-Al共掺均可较大程度的提高纳米ZnO对酸性橙的光催化，降解效果。掺杂过渡金属离子可在ZnO中引入缺陷位，形成中间能带，进而扩大ＺｎＯ的光吸收范围，以提高其光催化活性，但对于过渡金属离子掺杂的纳米ＺｎＯ却鲜有报道。
技术实现思路
本专利技术所要解决...
【技术保护点】
一种Co/ZnO复合材料的制备方法，包括如下步骤：将53gZnCl2、2gCoCl2·6H2O和43gNaOH分别溶解于100mL的去离子水中，再将3种溶液于磁力搅拌条件下充分混合，20min后移入高压反应釜中，在105‑115℃下反应8‑10h后，将反应釜内产物用去离子水和无水乙醇各洗涤3次后离心处理，于70‑75℃真空干燥箱中干燥8‑10h，即得。
【技术特征摘要】
1.一种Co/ZnO复合材料的制备方法，包括如下步骤：将53gZnCl2、2gCoCl2·6H2O和43gNaOH分别溶解于100mL的去离子水中，再将3种溶液于磁力搅拌条件下充...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。