Artificial turf grass leaf baking and shaping process
The invention discloses an artificial turf baking shaping process, which comprises the following steps: (1): Grass injection molding; (2): the shape of the grass into the baking equipment; (3): baking equipment for cooling the bottom leaves bottom, top of the baking equipment on the leaves of grass tip baking, baking temperature of 520 580 degrees Celsius, the baking time is 100 150 seconds, the grass is baked after melting, and the formation of spherical grass; (4): the grass out of baking equipment after baking, removed after cooling and forming of grass. The invention has the advantages of fast processing speed and high production efficiency.
【技术实现步骤摘要】
本专利技术涉及一种人造草坪加工
，具体讲是一种人造草坪草叶烘焙整形工艺。
技术介绍
绿化草坪是用多年生矮小草本植株密植，并经修剪的人工草地，而随着科技的进步，人造草坪被应用地越来越广泛。人造草坪是以仿草叶状的合成纤维，再植入机织的基布，背面涂上起固定作用的涂层以应用于运动场、庭园地坪和绿化地面上。人造草坪在生产过程中，当草叶成型后，需要对草叶的草尖进行处理，即将草尖的端部加工成圆球状，这样草叶摸上去就不会出现扎手的情况，人们摔倒在人造草坪上也不会出现扎痛的情况。然而，目前对草叶草尖的加工往往是用过后期手动加工或采用倒角设备对草叶草尖进行倒角，加工速度慢，工作效率低。
技术实现思路
鉴于上述现有技术的缺陷，本专利技术的目的在于：提供一种人造草坪草叶烘焙整形工艺，通过烘烤的方式对草叶草尖进行加工。本专利技术的技术解决方案是：人造草坪草叶烘焙整形工艺，包括以下步骤：(1)：将草叶一体注塑成型；(2)：将成型的草叶放入烘烤设备里；(3)：烘烤设备的底部对草叶底部进行冷却，烘烤设备的顶部对草叶草尖进行烘烤，烘烤的温度为520-580摄氏度，烘烤时间为100-150秒，草尖被烘烤后融化，并形成圆球状草尖；(4)：将烘烤完毕的草叶移出烘烤设备，移出后对草叶进行冷却成型。进一步地，烘烤的温度为550摄氏度，烘烤时间为120秒。应用本专利技术所提供的人造草坪草叶烘焙整形工艺，其有益效果是：通过烘烤的方式对草叶草尖进行加工，能够一次性处理大面积的草叶，加工速度快，生产效率高。附图说明图1为本专利技术的草叶在烘烤设备里烘烤时的原理示意图。具体实施方式为比较直观、完整地理解本...
【技术保护点】
人造草坪草叶烘焙整形工艺，其特征在于包括以下步骤：(1)：将草叶一体注塑成型；(2)：将成型的草叶放入烘烤设备里；(3)：烘烤设备的底部对草叶底部进行冷却，烘烤设备的顶部对草叶草尖进行烘烤，烘烤的温度为520‑580摄氏度，烘烤时间为100‑150秒，草尖被烘烤后融化，并形成圆球状草尖；(4)：将烘烤完毕的草叶移出烘烤设备，移出后对草叶进行冷却成型。
【技术特征摘要】
1.人造草坪草叶烘焙整形工艺，其特征在于包括以下步骤：(1)：将草叶一体注塑成型；(2)：将成型的草叶放入烘烤设备里；(3)：烘烤设备的底部对草叶底部进行冷却，烘烤设备的顶部对草叶草尖进行烘烤，烘烤的温度为520-580摄氏度，烘烤...