The invention is a kind of economic type elevator counterweight system, including steel cage skeleton, casting filling, the casting filling material comprises the following raw materials in weight portion: 95 smelting slag 112, barite 23 cement 9 39 copies, 15 copies, the amount of water. The invention adopts the industrial development of smelting slag instead of iron casting, reduce production costs, saving the iron ore resources; at the same time, the porous structure of industrial slag to combine with other components, the overall strength is high, the price is about 800 yuan / ton, equivalent to the cast iron counterweight blocks 1/5 and 1/2 composite counterweight reduce weight, cost, meet the economic requirements of the counterweight counterweight.
【技术实现步骤摘要】
本专利技术涉及配重块，具体的说是涉及一种经济型电梯配重块。
技术介绍
电梯配重块是电梯对重系统的核心部件，用于轿厢平衡。复合对重是在传统铸铁对重块基础上开发出来的，复合材料包括重晶石和铁矿石、钢材、水泥、水。伴随着矿山资源的开发，铁矿石日渐紧缺。
技术实现思路
为了解决上述问题，本专利技术提供了一种利用工业炉渣生产配重产品，降低配重成本,满足配重要求的经济型配重块。为了达到上述目的，本专利技术是通过以下技术方案实现的：本专利技术是一种经济型电梯配重块，包括钢筋制笼状骨架，浇铸填充物，所述浇铸填充物包括如下重量份的原料：冶炼炉渣95-112份，重晶石23-39份，水泥9-15份，适量水。2、根据权利要求1所述一种经济型电梯配重块，其特征在于：所述电梯配重块的制备工艺包括如下步骤：（1）将上述成分按比配置，输送至搅拌机内搅拌混合均匀，再输送到各个放料斗机内，振动浇铸至钢筋骨架内；（2）固化成型；（3）再送入锅炉蒸汽房内蒸汽养护。本专利技术的有益效果是：本专利技术采用工业冶炼炉渣代替铁矿石一体浇铸成型，降低了生产成本，节约了铁矿资源；同时工业炉渣的多孔结构有利于与其他成分结合，整体强度高，该产品价格约为800元/吨，相当于铸铁配重块的1/5、复合配重块的1/2，降低配重成本,满足配重要求的经济型配重块。具体实施方式为了加深对本专利技术的理解，下面将结合实施例对本专利技术做进一步详细描述，该实施例仅用于解释本专利技术，并不对本专利技术的保护范围构成限定。如实施例所示，本专利技术是一种经济型电梯配重块，包括钢筋制笼状骨架，浇铸填充物，所述浇铸填充物包括如下重量份的原料...
【技术保护点】
一种经济型电梯配重块，包括钢筋制笼状骨架，浇铸填充物，其特征在于：所述浇铸填充物包括如下重量份的原料：冶炼炉渣95‑112份，重晶石23‑39份，水泥9‑15份，适量水。
【技术特征摘要】
1.一种经济型电梯配重块，包括钢筋制笼状骨架，浇铸填充物，其特征在于：所述浇铸填充物包括如下重量份的原料：冶炼炉渣95-112份，重晶石23-39份，水泥9-15份，适量水。2.根据权利要求1所述一种经济型电...
【专利技术属性】
技术研发人员：黄业华，
申请(专利权)人：宣城市华菱精工科技股份有限公司，
类型：发明
国别省市：安徽;34